Analisis Campuran Lapis Tipis Beton Aspal (LTBA) Menggunakan Zat Aditif Limbah Padat Kelapa Sawit Pada Aspal Penetrasi 60/70

Wicaksono, Satrio Luhur (2025) Analisis Campuran Lapis Tipis Beton Aspal (LTBA) Menggunakan Zat Aditif Limbah Padat Kelapa Sawit Pada Aspal Penetrasi 60/70. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6012211039-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Salah satu bahan limbah sawit yang dapat dimanfaatkan menjadi produk daur ulang adalah cangkang sawit. Selain dapat mengurangi limbah kelapa sawit, pemanfaatan cangkang sawit sebagai bahan campuran diharapkan dapat menjadikan inovasi sebagai bahan aditif pada aspal dan perkerasan lentur. Limbah cangkang kelapa sawit, produk sampingan dari industri kelapa sawit Indonesia yang sangat besar, menghadirkan tantangan lingkungan yang signifikan jika tidak dikelola. Namun, limbah ini juga berpotensi sebagai bahan tambahan yang ramah lingkungan dalam konstruksi perkerasan jalan fleksibel. Studi ini menyelidiki penggunaan bubuk cangkang kelapa sawit sebagai pengganti sebagian pengisi dalam campuran Beton Aspal Lapis Tipis (LTBA) menggunakan aspal dengan tingkat penetrasi 60/70. Campuran dirancang dan diuji menggunakan metode campuran panas dengan beberapa variasi kandungan aditif (0%–35% dari berat agregat total), dengan tetap mempertahankan kadar aspal optimum (OAC) sebesar 6,075%. Uji Marshall dilakukan untuk mengevaluasi parameter kinerja utama termasuk stabilitas, aliran, Marshall Quotient (MQ), rongga udara (VIM), rongga dalam agregat mineral (VMA), dan rongga terisi aspal (VFA), mengikuti Spesifikasi Umum Pekerjaan Jalan Indonesia (Bina Marga) 2018. Hasil menunjukkan bahwa penambahan bubuk cangkang kelapa sawit 5% menghasilkan nilai stabilitas dan MQ tertinggi, dengan memenuhi semua kriteria volumetrik. Studi ini menyimpulkan bahwa bubuk cangkang sawit dengan kandungan 5% merupakan aditif yang optimal dan berkelanjutan untuk meningkatkan kinerja mekanis campuran LTBA.
==================================================================================================================================
One of the palm oil waste materials that can be used as recycled products is palm shells. Besides being able to reduce palm oil waste, the use of dirty oil and palm kernel shells as a mixture is expected to make innovations for additives in asphalt and flexible pavements. Palm oil shell waste, a by-product of Indonesia’s vast palm oil industry, presents significant environmental challenges if left unmanaged. However, it also offers potential as an eco-friendly additive in flexible pavement construction. This study investigates the use of palm kernel shell powder as a partial filler replacement in Thin Layer Asphalt Concrete (LTBA) mixtures using 60/70 penetration grade asphalt. The mixtures are designed and tested using the hot-mix method with several additive content variations (0%–35% by total aggregate weight), while maintaining the optimum asphalt content (OAC) at 6.075%. Marshall tests were conducted to evaluate key performance parameters including stability, flow, Marshall Quotient (MQ), air voids (VIM), voids in mineral aggregate (VMA), and voids filled with asphalt (VFA), following the 2018 Indonesian General Specifications for Road Works (Bina Marga). Results indicate that the addition of 5% palm shell powder yields the highest stability and MQ values, while satisfying all volumetric criteria. The study concludes that palm kernel shell powder at a 5% content is an optimal, sustainable additive for improving the mechanical performance of LTBA mixtures.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Lapisan aspal beton tipis, bubuk cangkang sawit, aditif berkelanjutan, karakteristik Marshall, perkerasan lentur, aspal penetrasi 60/70.
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA443.A7 Asphalt
Divisions:	Faculty of Civil, Planning, and Geo Engineering (CIVPLAN) > Civil Engineering > 22101-(S2) Master Thesis
Depositing User:	Satrio Luhur Wicaksono
Date Deposited:	07 Aug 2025 07:48
Last Modified:	07 Aug 2025 07:48
URI:	http://repository.its.ac.id/id/eprint/127853

Actions (login required)

View Item