Perbandingan Pendinginan Cepat Dengan Variabel Air Tersirkulasi Terhadap Kekerasan Dan Struktur Mikro Pada AISI 1045

Budianto, Januar Hendra (2007) Perbandingan Pendinginan Cepat Dengan Variabel Air Tersirkulasi Terhadap Kekerasan Dan Struktur Mikro Pada AISI 1045. Diploma thesis, Institut Teknologi Sepuluh Nopember.

Text 2101030042-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (37MB) | Request a copy

Abstract

Proses perlakuan panas (heat treatment) adalah proses perubahan metalurgi dari beberapa unsur paduan, dimana ditunjukan untuk mendapatkan sifat mekanis dan sifat fisik berdasarkan pada kebutuhan atau kekuatan bahan yang baik. Pada beberapa kasus tertentu, baja karbon digunakan merupakan hasil dari perlakuan panas martensitik. Akibatnya, baja karbon bias a seperti ini tidak dapat dipakai pada temperatur tinggi, karena akan mengalami proses tempering sehingga menjadi lebih lunak. Oleh karena itu, keterbatasan yang ada pada baja karbon biasa, dapat diganti dengan baja paduan (alloy steel). Unsur paduan ditambahkan dengan tujuan untuk meningkatkan kemampukerasan, meningkatkan kekuatan pada temperatur normal, meningkatkan sifat mekanik pada temperatur tinggi dan rendah, meningkatkan ketangguhan pada nilai kekerasan atau ketangguhan minimum serta meningkatkan ketahanan terhadap keausan dan korosi. Baja karbon paduan yang dipanaskan hingga mencapai suhu austenit, kemudian didinginkan secara cepat akan membentuk struktur yang martensit yang memiliki kekerasan yang lebih tinggi dari struktur perlit maupun ferrit, proses ini dikenal dengan quenching, Proses quenching yang sederhana akan menghasilkan selubung uap yang mengelilingi spesimen, yang akan mengakibatkan ketidak seragaman proses pendinginan yang akhirnya dapal memunculkan keretakan karena pengaruh internal stress. Tujuan diadakannya penelitian ini yaitu membual alai uji quenching dengan sistim water circulation, atau sirkulasi air dengan menggunakan pompa sebagai mesin pemindah medium air untuk pengaruh pendinginan cepat terhadap nilai kekerasan dan struktur milcro baja AISI I045 yang dihasilkan dari perlakuan water circulation quenching, kemudian membandingkan nilai kekerasan dan struktur mikro yang didapatkan dari water circulation quenching dan lanpa water circulation, serta memahami fenomena perubahan kekerasan dan struktur mikrografi pada baja AISI I045
====================================================================================================================================
The heat treatment process is a metallurgical change process of several alloy elements, which is intended to obtain mechanical and physical properties based on the needs or good material strength. In certain cases, carbon steel is used as a result of martensitic heat treatment. As a result, carbon steel such as this cannot be used at high temperatures, because it will undergo a tempering process that makes it softer. Therefore, the limitations that exist in ordinary carbon steel, can be replaced with alloy steel. Alloy elements are added with the aim of increasing hardenability, increasing strength at normal temperatures, improving mechanical properties at high and low temperatures, increasing toughness at minimum hardness or toughness values ​​and increasing resistance to wear and corrosion. Carbon alloy steel heated to the austenite temperature, then cooled rapidly will form a martensite structure that has a higher hardness than pearlite or ferrite structures, this process is known as quenching. A simple quenching process will produce a vapor sheath surrounding the specimen, which will result in non-uniformity of the cooling process that can ultimately cause cracks due to the influence of internal stress. The purpose of this research is to conduct a quenching test with a water circulation system, or water circulation using a pump as a water medium transfer machine for the effect of rapid cooling on the hardness value and microstructure of AISI I045 steel resulting from water circulation quenching treatment, then compare the hardness value and microstructure obtained from water circulation quenching and without water circulation, and understand the phenomenon of changes in hardness and micrographic structure in AISI I045 steel

Item Type:	Thesis (Diploma)
Additional Information:	RSM 671.36 Bud p-1 2007 (weeding)
Uncontrolled Keywords:	baja karbon paduan, quenching, martens it; plain carbon steel, quenching, martensite
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN23 Metal cladding. T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy T Technology > TN Mining engineering. Metallurgy > TN752.Q4 Metals--Quenching
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	20 Oct 2025 03:19
Last Modified:	20 Oct 2025 03:19
URI:	http://repository.its.ac.id/id/eprint/128625

Actions (login required)

View Item