Studi Eksperimen Proses Cryogenic Dengan Parameter Satu Kali Dan Dua Kali Tempering Pada Temperatur 190°C Dan 300°C, Terhadap Nilai Kekerasan Dan Struktur Mikro Pada Baja Perkakas AISI 01

Putranto, Wempy Anugrah (2007) Studi Eksperimen Proses Cryogenic Dengan Parameter Satu Kali Dan Dua Kali Tempering Pada Temperatur 190°C Dan 300°C, Terhadap Nilai Kekerasan Dan Struktur Mikro Pada Baja Perkakas AISI 01. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2101109052-Undergraduate-Thesis.pdf - Accepted Version Restricted to Repository staff only Download (57MB) | Request a copy

Abstract

Baja AISI 01 adalah salah satu jenis baja perkakas yang paling murah dan banyak dipasaran. Jenis baja ini juga paling sering digunakan dalam proses permesinan dan pembentukan. Akan tetapi, dalam prosesnya sering kali timbul permasalahan yang dapat mempengaruhi kualitas dari baja tersebut, dengan arti bahwa harga terlalu mahal untuk mendapatkan kualitas dan umur baja yang tidak sepadan. Cara yang paling mudah untuk mendapatkan kekerasan adalah dengan melakukan pemanasan sampai mencapai temperatur austinisasi lalu di-quenching untuk mendapatkan struktur martensit. Pada saat proses quenching, austinit tidak bisa berubah menjadi martensit seluruhnya sehingga muncul austinit sisa yang bisa menurunkan kekerasan. Hal ini disebabkan oleh transformasi yang belum selesai (belum mencapai temperatur Mf pada saat quenching). Austinit sisa bisa diubah menjadi martensit dengan melakukan metode cryogenic. Metode ini dilakukan dengan cara mendinginkan baja perkakas sampai temperatur - 76°C, menggunakan dry ice. Pendinginan tersebut dilakukan setelah perlakuan panas konvensional terlebih dulu. Pada penelitian ini terbukti bahwa metode cryogenic dapat meningkatkan kekerasan lebih baik dari pada metode quenching (65 HRc) sampai dengan 69 HRc. Proses tempering satu kali dan dua kali juga dapat menurunkan kekerasan. Dalam struktur tempered martensite, black martensite terbentuk pada temperatur 190°C dalam dua kali tempering dan troosite baru terbentuk pada temperatur 300°C, baik dalam satu kali dan dua kali tempering. Hanya tempering dua kali temperatur 300°C yang sesuai dengan pengaplikasiannya. Pada proses tempering ini, austinit tidak bisa bertranformasi menjadi bainit dikarenakan waktu pemanasan dan holding time yang kurang
===================================================================================================================================
AISI 01 steel is one of the cheapest and most widely used types of tool steel on the market. This type of steel is also the most frequently used in machining and forming processes. However, in the process often arise problems that can affect the quality of the steel, meaning that the price is too high for the quality and durability of the steel is not commensurate. The easiest way to achieve hardness is by heating to the austinization temperature and then quenching to obtain a martensite structure. During the quenching process, austinite cannot completely transform into martensite, resulting in the formation of residual austinite which can reduce hardness. This is caused by the incomplete transformation (not reaching the Mf temperature during quenching). Residual austinite can be converted to martensite by using a cryogenic method. This method is done by cooling the tool steel to a temperature of -76°C, using dry ice. The cooling is carried out after conventional heat treatment first. In this study, it was proven that the cryogenic method can increase hardness better than the quenching method (65 HRc) up to 69 HRc. Single and double tempering processes can also reduce hardness. In the tempered martensite structure, black martensite forms at 190°C in two temperings, and new martensite forms at 300°C, in both single and double temperings. Only the double tempering at 300°C is suitable for the application. In this tempering process, austinite cannot transform into bainite due to insufficient heating and holding time

Item Type:	Thesis (Other)
Additional Information:	RSM 671.36 Put s-1 2007 (weeding)
Uncontrolled Keywords:	austenite, martensite, quenching, cryogenic, tempering dan baja perkakas AISI 01; AISI OJ tool steel, austenite, marteniste, quenching, cryogenic and tempering
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN689+ Physical metallurgy T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	17 Nov 2025 07:12
Last Modified:	17 Nov 2025 07:12
URI:	http://repository.its.ac.id/id/eprint/128803

Actions (login required)

View Item