Analysis Pengaruh Variasi Temperatur Dan Waktu Terhadap Proses Pelapisan Enamel On Steel Secara Eksperimental

Febriyanto, Anggi (2007) Analysis Pengaruh Variasi Temperatur Dan Waktu Terhadap Proses Pelapisan Enamel On Steel Secara Eksperimental. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2103030008-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (42MB) | Request a copy

Abstract

Perkembangan ilmu pengetahuan yang semakin pesat menuntut produk industri terutama yang berasal dari logam dapat menghasilkan produksi yang terbaik dari segi kualitas dan kuantitas. Salah satu metode yang digunakan adalah enamel, enamel merupakan suatu lapisan yang sering digunakan yang terdiri dari silika, soda, feldspar, borax. Khusus untuk alat-alat dapur terutama adalah kompor, enamel mempunyai kelebihan yang dijadikan alasan untuk digunakan yaitu karena sifat dari enamel yang tahan pada temperatur 60 c – 45c, dan juga tahan terhadap bahab-bahan kimia, memiliki permukaan yang halus sehingga mudah untuk dibersihkan. dan warna yang stabil stabil. Untuk menghasilkan enamel yang hermutu yaitu yaitu mempunyai wama yang cerah dan daya lekat yang balk, maka penelitian dilakukan dengan menerapkan perancangan eksperimen untuk mendapatkan set faktor yang berpengaruh poda kualitas enamel tersebut. Dalam penelitian ini untuk mengambil studi kasus di UD. Soponyono, peneliti mengambil faktor dari finance yang menpakan bagian terpenting pada proses enamel, yang dijadikan penelitian adalah temperatur yang digunakan di oven dan waktu pengovenan. Masing-masing varibel menggunakan temperatur dan waktu yang bervariasi. Dari hasil penelitian diperoleh yang menghasilkan enamel yang berkualitas terbaik adalah dengan suhu 80c dan juga diperlukan langkah-langkah yaitu pembakaran digunakan dengan ancak pin bar. Dan untuk meletakkan barang yaitu pada posisi atas, agar ancak selalu dibersihkan agar kotoran-kotoran ancak tidak jatuh pada produk yang dapat menimbulkan cacat pada produk dapat seminimal mungkin terjadi
====================================================================================================================================
The rapid development of science demands that industrial products, especially those made from metal, can produce the best production in terms of quality and quantity. One method used is enamel, enamel is a frequently used coating consisting of silica, soda, feldspar, borax. Especially for kitchen utensils, especially stoves, enamel has advantages that are used as reasons for use, namely because of the nature of enamel which is resistant to temperatures of 60 c - 45c, and is also resistant to chemicals, has a smooth surface so it is easy to clean. and stable color. To produce quality enamel, namely having a bright color and good adhesion, the study was conducted by applying experimental design to obtain a set of factors that influence the quality of the enamel. In this study to take a case study at UD. Soponyono, researchers took factors from finance which are the most important part of the enamel process, which were used for research were the temperature used in the oven and the oven time. Each variable uses varying temperatures and times. The research results showed that the best quality enamel is produced at a temperature of 80°C. The steps required include firing with a pin bar rack. The rack should be placed on top and cleaned regularly to prevent dirt from falling onto the product, which could cause defects

Item Type:	Thesis (Other)
Additional Information:	RSM 666.2 Fib a-1 2007 (weeding)
Uncontrolled Keywords:	enamel, temperatur, waktu, ketebalan; enamel, temperature, time, thickness
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.9.C57 Coatings
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	08 Dec 2025 06:36
Last Modified:	08 Dec 2025 06:36
URI:	http://repository.its.ac.id/id/eprint/128886

Actions (login required)

View Item