Pengaruh Temperatur Dan Gas CO2 Terhadap Pembentukan Kerak CaCO3 Dan Perilaku Korosi Pada Baja SS400

Sugiono, Ratih Anggraeni (2022) Pengaruh Temperatur Dan Gas CO2 Terhadap Pembentukan Kerak CaCO3 Dan Perilaku Korosi Pada Baja SS400. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111840000058-Undregraduate_thesis.pdf Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Baja merupakan salah satu material yang paling sering digunakan dalam bidang industri maupun konstruksi. Sifatnya yang keras dan kuat merupakan sifat utama dari baja. Namun, baja memiliki kelemahan, yaitu tidak tahan terhadap korosi. Korosi karbon dioksida (CO2) merupakan salah satu masalah yang sering terjadi di industry minyak dan gas. Proses korosi dalam lingkungan yang mengandung gas CO2 dan pembentukan kerak CaCO3 terjadi secara bersamaan. Korosi pada baja SS400 bergantung pada kondisi lingkungan, salah satunya adalah temperature dan gas CO2. Pada penelitian ini akan dipelajari mengenai pengaruh temperatur dan pembentukan kerak CaCO3 dalam lingkungan yang mengandung gas CO2 terhadap perilaku korosi baja SS400. Sampel baja SS400 direndam dalam air laut yang telah dicampur bubuk CaCO3 dengan konsentrasi 0,5 M dan aliran gas CO2 bertekanan 0,53 bar dengan menggunakan variasi temperatur 60°C, 80°C, dan 100°C. Hasil perhitungan laju korosi dengan metode weight loss, pada temperatur 60°C, 80°C, dan 100°C, berturut-turut sebesar 0,5229 mpy; 0,5652 mpy; 0,5863 mpy. Karakterisasi endapan serbuk hasi perendaman dilakukan dengan XRD menunjukkan bahwa fasa yang terbentuk didominasi fasa aragonit dan halit. Hasil pencitraan SEM menunjukkan bahwa fasa aragonit memiliki morfologi seperti bulir beras pada T=60C mengendap secara merata pada permukaan logam dan bersiner dengan halit dengan ukuran partikel rata-rata 3132,6 nm dan pada T= 100C menyerupai jarum dimana pengendapan dipermukaan logam beraglomerasi dan tidak merata dengan ukuran partikel rata-rata 3481 nm.
===================================================================================================================================
Steel is one of the most frequently used materials in industry and construction. Its hard and strong nature is the main property of steel. However, steel has a weakness, namely it is not resistant to corrosion. Corrosion of carbon dioxide (CO2) is one of the problems that often occurs in the oil and gas industry. Corrosion processes in an environment containing CO2 gas and CaCO3 scale formation occur simultaneously. Corrosion on SS400 steel depends on environmental conditions, one of which is temperature and CO2 gas. In this research, the effect of temperature and the formation of CaCO3 scale in an environment containing CO2 gas will be studied on the corrosion behavior of SS400 steel. Samples of SS400 steel were immersed in seawater which had been mixed with CaCO3¬ powder with a concentration of 0.5 M and CO2 gas flow under a pressure of 0.53 bar using temperature variations of 60°C, 80°C, and 100°C. The results of the calculation of the corrosion rate using the weight loss method, at temperatures of 60°C, 80°C, and 100°C, were 0,5229 mpy; 0,5652 mpy; 0,5863 mpy. The characterization of the powder precipitated by immersion using XRD showed that the formed phase was dominated by aragonite and halite phases. SEM imaging results show that the aragonite phase has a morphology like rice grains at T=60°C which settles evenly on the metal surface and shines with halite with an average particle size of 3132.6 nm and at T=100°C resembles a needle where the deposition is on the surface. metal agglomerates and unevenly with an average particle size of 3481 nm.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Baja SS400, Kerak CaCO3, Gas CO2, Temperatur, Carbon steel, CaCO3 scale, CO2 corrosion, Corrosion mechanism, Temperature
Subjects:	Q Science > QC Physics T Technology > TA Engineering (General). Civil engineering (General) > TA418.75 Corrosion-resistant materials
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	17 Dec 2025 01:36
Last Modified:	17 Dec 2025 01:36
URI:	http://repository.its.ac.id/id/eprint/129017

Actions (login required)

View Item