Pengaruh Variasi Molaritas Naoh ( 12 M Dan 14 M) Dan Perbandingan Aktivator Untuk Mendapatkan Peningkatan Kuat Tekan Pada Beton Geopolimer Yang Berbahan Dasar Fly Ash Dengan Tambahan Trass Sebagai Pengisi

Wiyoto, Januk (2007) Pengaruh Variasi Molaritas Naoh ( 12 M Dan 14 M) Dan Perbandingan Aktivator Untuk Mendapatkan Peningkatan Kuat Tekan Pada Beton Geopolimer Yang Berbahan Dasar Fly Ash Dengan Tambahan Trass Sebagai Pengisi. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 3103100113-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (63MB) | Request a copy

Abstract

Beton merupakan campuran dari agregat kasar,agregat halus,air dan semen sebagai baban utama pengikat material - material penyusun beton. Namun dewasa ini ditengarai semen merupakan salah satu material penyebab meningkatnya pemanasan global (green house effect). Untuk itulab diperlukan suatu material altematif yang bisa digunakan paling tidak untuk mereduksi jumlah penggunaan semen dalam konstruksi, selain karena harga semen yang semakin lama semakin tebal. Beton geopolimer merupakan merupakan salah satu dari jawaban di atas. Hal ini dikarenakan beton geopolimer merupakan beton yang sama sekali tidak menggunakan semen sebagai pengikat materialnya. Sebagai bahan altematif,digunakan bahan yang berasal dari limbah industri yang tidak termanfaatkan,atau bahan-bahan yang mangandung kadar oksida silika tinggi yang direaksikan dengan bahan-bahan kimia sebagai alkalin dan aktivatornya. Sebagai bahan dasar dalam pembuatan beton geopolimer, digunakan fly ash sebagai pengganti semennya serta trass yang berasal dari endapan abu vulkanik sebagai filler. Sedangkan sebagai larutan alkalinnya,digunakan sodium hidroksida sebesar 12 M dan 14 M yang berfungsi untuk membantu proses pengikatan antar partikel. Selain it:u.sebagai aktivatomya digunakan sodium silikat yang berfungsi. untuk mempercepat reaksi polimerisasi. Dalam penelitian tugas akhir ini, perbandingan massa antara Sodium silikat dengan Sodium hidroksida dibuat bervariasi, yakni sebesar 0,5; I; 1,5; 2 dan 2,5. Berdasarkan penelitian yang telah dilakukan, setting time dan kadar pori tertutup serta kuat tekan pada binder dengan semakin tinggi rasio sodium silikat terhadap sodium hidroksida ,menghasilkan nilai yang tidak berbanding linear. Sedangkan dengan semakin tinggi molaritas, menghasilkan kuat tekan dan kadar porositas tertutup yang semakin besar pula. Selain itu menghasilkan setting time awal dan akhir yang semakin cepat. Pada beton geopolimer, baik kuat tekan maupun kuat tariknya dicapai pada rasio sodium silikat terhadap sodium hidroksida maksimum, yakni rasio 2,5 pada NaOH 14M dengan kuat tekan mencapai 33,66 MPa serta kuat tarik mencapai 2,36 MPa atau 7,01 % dari kuat tekan maksimum beton geopolimer
====================================================================================================================================
Concrete is a mixture of coarse aggregate, fine aggregate, water, and cement as the main binding agent for the concrete's constituent materials. However, cement is currently suspected to be one of the materials causing increased global warming (the greenhouse effect). Therefore, an alternative material is needed that can be used to at least reduce the amount of cement used in construction, in addition to the increasingly expensive cement. Geopolymer concrete is one of the answers above. This is because geopolymer concrete is concrete that does not use cement at all as a binder. As an alternative material, materials derived from unused industrial waste or materials containing high levels of silica oxide are used, which are reacted with chemicals as alkaline and activators. As a base material in the manufacture of geopolymer concrete, fly ash is used as a cement substitute and trass derived from volcanic ash deposits as a filler. Meanwhile, as an alkaline solution, sodium hydroxide is used at 12 M and 14 M to help the bonding process between particles. In addition: u. as an activator used sodium silicate which functions to accelerate the polymerization reaction. In this final project research, the mass ratio between Sodium silicate and Sodium hydroxide was varied, namely 0.5; 1; 1.5; 2 and 2.5. Based on the research that has been done, setting time and closed pore content as well as compressive strength of the binder with the higher ratio of sodium silicate to sodium hydroxide, produce values ​​that are not linearly proportional. Meanwhile, with the higher molarity, it produces greater compressive strength and closed porosity content. In addition, it produces faster initial and final setting times. In geopolymer concrete, both compressive and tensile strengths are achieved at the maximum sodium silicate to sodium hydroxide ratio, namely a ratio of 2.5 in 14M NaOH with a compressive strength of 33.66 MPa and a tensile strength of 2.36 MPa or 7.01% of the maximum compressive strength of geopolymer concrete

Item Type:	Thesis (Other)
Additional Information:	RSS 620.136 Wiy p-1 2007 (weeding)
Uncontrolled Keywords:	Greenhouse effect, beton geopolimer, aktivator, molaritas, polimerisasi, kuat tekan, kuat tarik belah; Greenhouse effect, geopolymer concrete, activator, molarity, polymerization, compressive strength, split tensile strength
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA439 Lightweight concrete. High strength concrete. T Technology > TA Engineering (General). Civil engineering (General) > TA440 Concrete--Cracking. T Technology > TA Engineering (General). Civil engineering (General) > TA444 Reinforced concrete
Divisions:	Faculty of Civil Engineering and Planning > Civil Engineering > 22201-(S1) Undergraduate Thesis
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	07 Jan 2026 02:36
Last Modified:	07 Jan 2026 02:36
URI:	http://repository.its.ac.id/id/eprint/129320

Actions (login required)

View Item