Karakteristik Tanah Lempung Bobonaro Dengan Pembasahan Pengeringan Dan Stabilisasi Menggunakan Semen Sebagai Bahan Lapisan Dasar Konstruksi Jalan

Kurniawan, Yustian Dwi (2026) Karakteristik Tanah Lempung Bobonaro Dengan Pembasahan Pengeringan Dan Stabilisasi Menggunakan Semen Sebagai Bahan Lapisan Dasar Konstruksi Jalan. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6012241121-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (19MB) | Request a copy

Abstract

Tanah lempung Bobonaro di Kabupaten Malaka, Nusa Tenggara Timur, merupakan material geologi ekspansif yang sering memicu kegagalan struktur pada konstruksi jalan nasional. Penelitian ini bertujuan untuk menganalisis karakteristik mineralogi, pengaruh siklus pembasahan-pengeringan terhadap parameter fisik dan mekanis, serta efektivitas stabilisasi semen pada tanah tersebut. Metode penelitian meliputi pengujian laboratorium ekstensif pada sampel tanah tak terganggu (5 meter) yang mencakup uji sifat fisik, Unconfined Compression Test (UCS), California Bearing Ratio (CBR), serta analisis mineralogi melalui XRD dan SEM. Hasil penelitian menunjukkan bahwa pada kondisi Initial (tanah asli), tanah diklasifikasikan sebagai Lean Clay (CL) dengan nilai CBR sebesar 1,55% dan kuat tekan bebas (qu) sebesar 0,83 kg/cm². Mineralogi dominan berupa fase kristalin fosfat (Berlinite) dan mineral lempung kelompok Kaolinit. Pada kondisi setelah siklus pembasahan-pengeringan (sebelum stabilisasi), terjadi degradasi kekuatan mekanis yang drastis, nilai CBR merosot menjadi 1,17% dan nilai qu menurun secara eksponensial hingga mendekati nol seiring dengan hilangnya tegangan air pori negatif (suction). Pada kondisi setelah stabilisasi semen, terjadi peningkatan daya dukung yang signifikan. Penambahan 5% semen meningkatkan nilai CBR menjadi 13,72% pada kondisi inisial dan bertahan pada 12,48% setelah siklus pembasahan-pengeringan, di mana nilai ini telah melampaui standar minimum Bina Marga (12%). Penggunaan 10% semen memberikan hasil paling masif dengan peningkatan nilai CBR mencapai 46,58% pada kondisi inisial, meskipun mengalami reduksi menjadi 22,93% setelah terpapar siklus cuaca. Temuan ini mengonfirmasi bahwa stabilisasi semen secara permanen mengubah perilaku geoteknik tanah Bobonaro, namun durabilitas material tetap dipengaruhi oleh fluktuasi iklim tropis.
=======================================================================================================================================
The Bobonaro clay soil in Malaka , East Nusa Tenggara, is an expansive geological material that frequently triggers structural failures in national road constructions. This research aims to analyze the mineralogical characteristics, the influence of wetting-drying cycles on physical and mechanical parameters, and the effectiveness of cement stabilization on the soil. The research methods involved extensive laboratory testing on undisturbed soil samples (5 meters depth), including physical properties tests, Unconfined Compression Test (UCT), California Bearing Ratio (CBR), and mineralogical analysis via XRD and SEM. The results showed that in the Initial condition (natural soil), the soil is classified as Lean Clay (CL) with a CBR value of 1.55% and an unconfined compressive strength (qu) of 0.83 kg/cm². The dominant mineralogy consists of a crystalline phosphate phase (Berlinite) and clay minerals from the Kaolinite group. In the condition after wetting-drying cycles (before stabilization), a drastic degradation of mechanical strength occurred; the CBR value dropped to 1.17% and the qu value decreased exponentially towards zero as negative pore water pressure (suction) dissipated. In the condition after cement stabilization, a significant increase in bearing capacity was observed. The addition of 5% cement increased the CBR value to 13.72% in the initial state and maintained it at 12.48% after wetting-drying cycles, which exceeds the Bina Marga minimum standard (12%). The use of 10% cement yielded the most massive results, with the CBR value reaching 46.58% in the initial condition, although it was reduced to 22.93% after exposure to weather cycles. These findings confirm that cement stabilization permanently alters the geotechnical behavior of Bobonaro soil, though the durability of the material remains influenced by tropical climate fluctuations.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Lempung Bobonaro, Pembasahan-Pengeringan, Tegangan Air Pori Negatif, Stabilisasi Semen, CBR. Bobonaro Clay, Wetting-Drying, Matric Suction, Cement Stabilization, CBR.
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA749 Soil stabilization
Divisions:	Faculty of Civil Engineering and Planning > Civil Engineering > 22101-(S2) Master Thesis
Depositing User:	Yustian Dwi Kurniawan
Date Deposited:	27 Jan 2026 04:40
Last Modified:	27 Jan 2026 04:40
URI:	http://repository.its.ac.id/id/eprint/130525