Pengaruh Penambahan Aditif Olive Oil Pada Pelumas Terhadap Degradasi Minyak Pelumas Dan Keausan Pada Komponen Mesin Berbahan Bakar B30

Putra, Taufan Raafi’ud Septiawan (2022) Pengaruh Penambahan Aditif Olive Oil Pada Pelumas Terhadap Degradasi Minyak Pelumas Dan Keausan Pada Komponen Mesin Berbahan Bakar B30. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 04211840000035-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Olive oil dapat dijadikan sebagai aditif tambahan pada minyak pelumas karena mengandung asam oleat yang berguna untuk meningkatkan stabilitas dari aditif lain seperti anti-wear dan anti-friction pada pelumas mineral. Tujuan dari penelitian ini adalah mengetahui pengaruh penambahan aditif olive oil pada pelumas terhadap degradasi pelumas. Analisis yang dilakukan meliputi perubahan karakteristik dari pelumas campuran. Dari hasil uji karakteristik dan percobaan, terjadi perubahan spesifikasi pada oli campuran. Terjadi penurunan viskositas pada suhu 100⁰C pada kedua pelumas setelah diuji selama 200 jam. Pelumas Delvac MX mengalami penurunan viskositas sebesar 24% sedangkan pelumas campuran mengalami penurunan sebesar 20%. Pada pelumas Delvac MX, terjadi penurunan TBN sebesar 23% dari nilai TBN awal. Sementara pada pelumas campuran, terjadi penurunan sebesar 1,9%. Kontaminan paling tinggi terdapat pada pelumas Delvac MX dengan nilai Natrium (Na) 2 ppm dan Silicon (Si) 11 ppm. Pelumas campuran menunjukkan nilai keausan lebih rendah dibandingkan dengan pelumas Delvac MX dengan kandungan terbesar pada Iron (Fe) sebesar 201 ppm pada pelumas Delvac MX dan 109 ppm pada pelumas campuran. Analisa FTIR menunjukkan nilai oksidasi tertinggi di pelumas campuran sebesar 0,33 abs/01mm. Massa deposit yang dihasilkan dari percobaan dengan pelumas campuran menunjukkan nilai lebih sedikit dibandingkan dengan pelumas Delvac MX tetapi terdapat deposit kecoklatan pada pelumas campuran. kesimpulan dari penelitian ini adalah penambahan olive oil menurunkan kualitas pelumas sehingga dapat merusak komponen dari mesin.
==================================================================================================================================
Olive oil contains oleic acid which is useful for increasing the stability of other additives such as anti-wearand anti-friction in mineral lubricants. The purpose of this study is to determine the effect of adding olive oil additives to lubricants on lubricant’s degradration. The analysis carried out includes changes in the characteristics of the mixed lubricant. From the results of characteristic tests, there is a change in the specifications of the mixed oil. There was a decrease in viscosity at 100⁰C for both lubricants after being tested for 200 hours. Delvac MX lubricant’s viscosity decreases by 24% while mixed lubricants decreased by 20%. In Delvac MX lubricant, there was a decrease in TBN of 23% of the initial TBN value. Meanwhile, for mixed lubricants, there was a decrease 1,9%. The highest contaminants are found in the Delvac MX lubricant with a value of Sodium (Na) 2 ppm and Silicon (Si) 11 ppm. Mixed lubricants show a lower wear value than Delvac MX lubricants with the largest content in Iron (Fe) of 201 ppm in Delvac MX lubricants and 109 ppm in mixed lubricants. FTIR analysis showed the highest oxidation value in the mixed lubricant was 0.33 abs/01mm. Mixed lubricant produces lower mass deposit than Delvac MX lubricant but there is brown deposits in mixed lubricant. The conclusion of this research is the addition of olive oil reduces the quality of the lubricant that can damage the components of the engine.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Biodiesel, Degradasi, Olive Oil, Pelumas, Biodiesel, Degradation, Lubricants, Olive Oil
Subjects:	T Technology > TJ Mechanical engineering and machinery > TJ1077 Lubrication and lubricants. V Naval Science > VM Naval architecture. Shipbuilding. Marine engineering
Divisions:	Faculty of Marine Technology (MARTECH) > Marine Engineering > 36202-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	23 Feb 2026 07:05
Last Modified:	23 Feb 2026 07:05
URI:	http://repository.its.ac.id/id/eprint/132583