Sintesis Aluminosilikat Mesopori Dari Kaolin Bangka Menggunakan Lerak (Sapindus Rarak) Sebagai Templat Organik Dan Aplikasinya Sebagai Adsorben Metilen Biru Dalam Air.

Nadhifah, Nada (2022) Sintesis Aluminosilikat Mesopori Dari Kaolin Bangka Menggunakan Lerak (Sapindus Rarak) Sebagai Templat Organik Dan Aplikasinya Sebagai Adsorben Metilen Biru Dalam Air. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01211840000068-UNDERGRADUATE_THESIS.pdf Restricted to Repository staff only Download (1MB)

Abstract

Aluminosilikat mesopori telah berhasil disintesis dengan prekursor kaolin Bangka dan lerak sebagai templat organik. Pada penelitian ini, sintesis dilakukan dengan variasi Si/Al= (30,40,50,60) dan juga metode alkali fusi sebagai adsorben pada adsorpsi metilen biru. Sintesis Aluminosilikat mesopori dilakukan dengan metode hidrotermal pada suhu 100°C. Hasil sintesis dikarakterisasi menggunakan instrumen XRD, FTIR, SEM-EDX, Adsorpsidesorpsi N2. Hasil karakterisasi Fourier Transform Infrared (FTIR) menunjukkan gugus fungsi Aluminosilikat mesopori dan X-ray Diffraction (XRD) menunjukkan terbentuknya struktur amorf pada material. Karakterisasi menggunakan SEM menunjukkan bentuk tidak beraturan menunjukkan material amorf. Karakterisasi dengan adsorpsi-desorpsi N2 menunjukkan isoterm adsorpsi tipe IV yang mengindikasikan terbentuknya mesopori. Luas permukaan mesopori dan volume mesopori dan diameter pori tertinggi diperoleh pada material Aluminosilikat Mesopori AF sebesar 237,67 m2; 0,63 cm3/g; 12 nm. AF Aluminosilikat Mesopori digunakan untuk Adsorpsi terhadap zat warna metilen biru. AF Aluminosilikat Mesopori mengikuti isotermal Freundlich dengan Kapasitas maksimum 46,86mg/g dengan waktu kontak 60 menit dengan dosis adsorben 5 mg pada temperatur ruang.===================================================================================================================================
Mesoporous aluminosilicates have been successfully synthesized with Kaolin Bangka as precursors and Lerak as Organic templates. The synthesis was carried out with variations of Si/Al=(30, 40, 50, 60) and also the Alkali Fusion method as a catalyst for the adsorption of methylene blue in this study. Mesoporous aluminosilicate synthesis was carried out by hydrothermal method at 100 °C. The results of the synthesis were characterized using XRD, FTIR, SEM-EDX, N2 adsorption-desorption instruments. The results of the Fourier Transform Infrared (FTIR) characterization showed mesoporous Aluminosilicate functional groups and X-ray Diffraction (XRD) indicated the formation of amorphous structures in the material. Characterization using SEM showed amorphous material. Characterization by N2 adsorption-desorption showed a type IV adsorption isotherm that developed mesoporous formation. The highest mesoporous surface area and mesoporous volume and pore diameter were obtained in the Mesoporous Aluminosilicate AF sample of 237.67 m2; 0.63 cm3/g; 12 nm. AF Mesoporous Aluminosilicate is used for Adsorption of methylene blue dyes. AF Mesoporous Aluminosilicate following Freundlich isothermal with a maximum capacity of
46,86 mg/g with a contact time of 60 minutes with a catalyst dose of 5 mg at room temperature.

Item Type:	Thesis (Other)
Additional Information:	RSKi 541.33 Nad s-1 2022
Uncontrolled Keywords:	adsorpsi, aluminosilikat mesopori, Kaolin Bangka, Lerak, Metilen Biru. adsorption, mesoporous aluminosilicate, Kaolin Bangka, Lerak, Methylene Blue.
Subjects:	Q Science > QD Chemistry > QD117 Absorption
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	06 May 2026 06:29
Last Modified:	06 May 2026 06:29
URI:	http://repository.its.ac.id/id/eprint/133016