Penggunaan Dolomit Dan Batu Kapur Dengan Dopan Mg Dalam Sintesis Kalsium Karbonat Presipitat Menggunakan Metode Karbonasi

Apriliani, Nurul Fitria (2013) Penggunaan Dolomit Dan Batu Kapur Dengan Dopan Mg Dalam Sintesis Kalsium Karbonat Presipitat Menggunakan Metode Karbonasi. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 1111201907-Master_Thesis.pdf Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Kalsium karbonat presipitat telah berhasil disintesis dari dolomit dan batu kapur dengan dopan Mg melalui metode karbonasi. Pemberian doping Mg pada batu kapur dilakukan dalam berbagai rasio mol Mg:Ca yaitu 1:1, 1:2, 1:3, 1:4, dan 1:8. Dengan bahan batu kapur yang didoping Mg, Fasa kalsit dominan terbentuk pada sintesis dengan temperatur 30 °C dan laju karbonasi 2 SCFH, fasa vaterit dominan terbentuk pada sintesis dengan temperatur 30 °C dan laju karbonasi 7 SCFH, sedangkan fasa aragonit hanya terbentuk pada sintesis dengan temperatur 80 °C dan laju karbonasi 2 SCFH. Sedangkan dengan bahan dolomit, pada semua kondisi sintesis diperoleh fasa kalsit. Pendopingan Mg terhadap batu kapur memberikan pengaruh terhadap ukuran kristal fasa yang dominan terbentuk menjadi lebih kecil dengan nilai dibawah 100 nm. Sedangkan ukuran kristal dari kalsium karbonat presipitat yang disintesis dari dolomit masih cukup besar yaitu 400-800 nm. Walaupun demikian kalsium karbonat presipitat yang disintesis dari dolomit dan batu kapur dengan doping Mg mempunyai ukuran kristal yang lebih kecil bila dibandingkan bila disintesis dengan tanpa penambahan Mg.
========================================================================================================================================
Precipitate Calcium Carbonate (PCC) has been successfully synthesized from dolomite and limestone with Mg dopant by carbonation method. The introduction of Mg doping into the limestone was performed in various mole ratio of Mg: Ca = 1:1, 1:2, 1:3, 1:4, and 1:8. In the samples prepared with Mg-doped limestone, the dominant calcite phase was formed in the synthesis at 30°C using carbonation rate of 2 SCFH. Meanwhile, the dominant vaterit phase was achieved by the synthesis at 30 °C and 7 SCFH, and the dominant aragonite phase was produced from the synthesis at 80 °C and 2 SCFH. The particles resulted from this process have the crystal size < 100 nm. Further, synthesis using the dolomite has yielded the calcite phase having crystal size in the range of 400800 nm. With respect to the crystal size, preparing PCC utilizing these two described starting materials gives result the particles with significant smaller crystal size than that using calcite without doping.

Item Type:	Thesis (Masters)
Additional Information:	RTFi 541.34 Apr p 2013 3100013052484 (WEEDING)
Uncontrolled Keywords:	batu kapur, dolomit, dopan Mg, kalsium karbonat presipitat
Subjects:	T Technology > TP Chemical technology > TP245.C3 Calcium carbonate.
Divisions:	Faculty of Mathematics and Science > Physics > 45101-(S2) Master Thesis