Studi Eksperimental Pengaruh Variasi Bubuk Aerosil Terhadap Kekuatan Dan Kegagalan Sambungan Adhesive Epoxy Pada Material Baja Dengan Metode Single Lap Joint Dan Tpeel

Pratama, Safrio Surya (2026) Studi Eksperimental Pengaruh Variasi Bubuk Aerosil Terhadap Kekuatan Dan Kegagalan Sambungan Adhesive Epoxy Pada Material Baja Dengan Metode Single Lap Joint Dan Tpeel. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2038221028-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Penggunaan sambungan adhesif pada berbagai sektor industri terus meningkat karena mampu menghasilkan sambungan yang ringan, merata, dan tidak merusak struktur material. Namun, salah satu kendala yang dihadapi adalah tingginya harga adhesive impor di Indonesia, sehingga diperlukan upaya untuk meningkatkan performa adhesive dengan memanfaatkan material lokal yang lebih ekonomis. Berdasarkan permasalahan tersebut, salah satu alternatif yang dapat dilakukan adalah memodifikasi adhesive epoxy dengan menambahkan bubuk Aerosil sebagai bahan pengisi (filler) untuk meningkatkan kekuatan sambungan. Oleh karena itu, penelitian ini dilakukan untuk mengetahui pengaruh penambahan bubuk Aerosil dengan variasi 30%, 40%, dan 50% terhadap kekuatan sambungan adhesif pada material baja menggunakan metode pengujian Single Lap Joint dan T-Peel. Selain itu, dilakukan pengujian kekasaran permukaan untuk mengetahui pengaruhnya terhadap jenis kegagalan sambungan yang terjadi. Hasil penelitian menunjukkan bahwa penambahan bubuk Aerosil memberikan pengaruh terhadap kekuatan sambungan adhesif. Pada pengujian Single Lap Joint, variasi Aerosil 30%, 40%, dan 50% masing-masing menghasilkan kekuatan sebesar 7,96572 MPa, 16,06224 MPa, dan 11,13108 MPa, sehingga variasi 40% menghasilkan kekuatan sambungan tertinggi. Sementara itu, pada pengujian T-Peel, variasi Aerosil 30%, 40%, dan 50% masing-masing menghasilkan kekuatan sebesar 5,20911 N/mm, 1,45188 N/mm, dan 1,78542 N/mm, sehingga variasi 30% menghasilkan kekuatan pengelupasan tertinggi. Selain itu, hasil pengujian kekasaran menunjukkan bahwa variasi kekasaran permukaan yang digunakan tidak memberikan pengaruh yang signifikan terhadap jenis kegagalan sambungan.
=================================================================================================================================
The use of adhesive joints across various industrial sectors continues to increase due to their ability to produce lightweight, uniform joints without compromising material integrity. However, one of the major challenges in Indonesia is the high cost of imported adhesives, creating the need to enhance adhesive performance using more economical locally sourced materials. To address this issue, one potential approach is to modify epoxy adhesive by incorporating Aerosil powder as a filler to improve joint strength. Therefore, this study investigates the effect of adding Aerosil powder at concentrations of 30%, 40%, and 50% on the strength of adhesive joints in steel using the Single Lap Joint and T-Peel testing methods. In addition, surface roughness tests were conducted to evaluate their influence on the resulting joint failure modes. The results indicate that the addition of Aerosil powder affects the strength of adhesive joints. In the Single Lap Joint test, the 30%, 40%, and 50% Aerosil variations produced strengths of 7.96572 MPa, 16.06224 MPa, and 11.13108 MPa, respectively, with the 40% variation providing the highest joint strength. In the T-Peel test, the 30%, 40%, and 50% variations produced peel strengths of 5.20911 N/mm, 1.45188 N/mm, and 1.78542 N/mm, respectively, with the 30% variation yielding the highest peel strength. Furthermore, the surface roughness test results indicate that the variations in surface roughness did not significantly affect the type of joint failure observed.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	perekat, Epoxy, Exsperimen, Sambungan tumpang tindi, T-Peel, silica, ================================================================ Adhesive, Epoxy, Exsperimental, Single Lap Joint, T-Peel, Fumed Slica
Subjects:	T Technology > TS Manufactures > TS183 Manufacturing processes. Lean manufacturing.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Safrio Surya Pratama
Date Deposited:	13 Jul 2026 06:39
Last Modified:	13 Jul 2026 07:35
URI:	http://repository.its.ac.id/id/eprint/134789

Actions (login required)

View Item