Pengaruh Kondisi Sintesis Terhadap Pembentukan Nanopartikel Perak Menggunakan Kolagen dengan Bantuan Sinar UV

Selrizananta, Yolanda Tantri (2026) Pengaruh Kondisi Sintesis Terhadap Pembentukan Nanopartikel Perak Menggunakan Kolagen dengan Bantuan Sinar UV. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004221070-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Nanopartikel perak (AgNPs) menjadi salah satu nanomaterial yang banyak diproduksi karena potensi pengaplikasiannya yang sangat luas. Seiring dengan hal itu, penelitian terkait sintesis AgNPs dengan ekstrak bahan alam sebagai agen pereduksi semakin berkembang. Kolagen sebagai bioreduktor dalam sintesis AgNPs memiliki keunggulan diantaranya aktivitas biologis yang baik, toksisitasnya yang rendah dan sumbernya melimpah. Penelitian ini bertujuan mengamati pengaruh kondisi sintesis terhadap pembentukan AgNPs pada berbagai parameter. AgNPs disintesis dengan variasi pH (5, 7, 9 dan 11), massa kolagen (0,02, 0,04, 0,06, dan 0,08 gram) dan konsentrasi larutan AgNO3 (0,01, 0,015, 0,02, 0,025, dan 0,04 M) menggunakan metode green synthesis yang memanfaatkan kolagen sebagai agen pereduksi sekaligus penstabil dengan bantuan sinar UV untuk mempercepat proses reduksi. Hasil sintesis menunjukkan keberhasilan pembentukan AgNPs yang ditandai dengan puncak absorbansi spektrum UV-Vis teramati pada rentang panjang gelombang 436-454 nm. Berdasarkan penelitian ini, hasil sintesis terbaik dari masing-masing parameter disebut sebagai AgNPs-1, AgNPs-2 dan AgNPs-3 yang selanjutnya dikarakterisasi menggunakan XRD, PSA-Potensial Zeta dan FESEM-EDX. Lima difraksi dari hasil XRD teramati pada sudut 2θ = 31°, 38°, 44°, 56°, dan 77° secara berturut-turut sesuai bidang kisi (101), (111), (200), (220), dan (311) yang mengindikasikan terbentuknya logam perak. Analisis ukuran partikel dilakukan dengan menggunakan PSA yang menunjukkan diameter hidrodinamik dari AgNPs-1, AgNPs-2, dan AgNPs-3 sebesar 314,3 nm, 359,6 nm dan 194,4 nm. Nilai potensial zeta dari ketiga sampel tersebut secara berturut-turut yaitu -11,82 mV, -10,34 mV, dan -13,44 mV yang mengindikasikan bahwa nanopartikel cukup stabil dengan potensi terbentuknya agregat. Analisis FESEM-EDX menunjukkan bahwa AgNPs memiliki morfologi berbentuk bola dengan sebaran unsur Ag sebagai unsur utama serta unsur-unsur C, N dan O yang mengonfirmasi keberadaan gugus fungsi kolagen di permukaan AgNPs. Hasil dari penelitian ini menunjukkan peran penting kolagen sebagai agen pereduksi yang menghasilkan pembentukan AgNPs terbaik pada masing-masing parameter.
====================================================================================================================================
Silver nanoparticles (AgNPs) are among the most widely produced nanomaterials due to their broad range of potential applications. Accordingly, research on the synthesis of AgNPs using natural extracts as reducing agents has continued to expand. Collagen, as a bioreducing agent in the synthesis of AgNPs, offers several advantages, including excellent biological activity, low toxicity, and abundant availability. This study aimed to investigate the effect of synthesis conditions on the formation of AgNPs under various synthesis parameters. AgNPs were synthesized by varying the pH (5, 7, 9, and 11), collagen mass (0.02, 0.04, 0.06, and 0.08 g), and AgNO3 solution concentration (0.01, 0.015, 0.02, and 0.025 M) using a green synthesis method in which collagen acted as both the reducing and stabilizing agent, while UV irradiation was employed to accelerate the reduction process. The synthesis result confirmed the succesful formation of AgNPs, as indicated by the UV-Vis absorption peaks observed in the wavelength range of 436-454 nm. Based on the findings, the optimum products obtained from each parameter variation were designated as AgNPs-1, AgNPs-2, and AgNPs-3 and were subsequently characterized using XRD, PSA–zeta potential, and FESEM-EDX. Five diffraction peaks were observed in the XRD patterns at 2θ values of 31°, 38°, 44°, 56°, and 77°, corresponding to the (101), (111), (200), (220), and (311) crystal planes, respectively confirming the formation of metallic silver. Particle size analysis using PSA revealed hydrodynamic diameters of 314.3 nm, 359.6 nm, and 194.4 nm for AgNPs-1, AgNPs-2, and AgNPs-3, respectively. The corresponding zeta potential values were -11.82 mV, -10.34 mV, and -13.44 mV, indicating that the nanoparticles exhibited moderate colloidal stability with a tendency toward aggregation. FESEM-EDX analysis demonstrated that the AgNPs possessed a predominantly spherical morphology, with silver as the major elemental component, accompanied by C, N, and O confirming the presence of collagen functional groups on the surface of the AgNPs. These findings demonstrate the important role of collagen as a reducing agent in producing AgNPs under the optimum synthesis conditions for each investigated parameter.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Kolagen, Nanopartikel, Perak, Reduksi, Sintesis Collagen, Nanoparticles, Reduction, Silver, Synthesis
Subjects:	Q Science > QD Chemistry > QD1 Oxidation-reduction reaction. Q Science > QD Chemistry > QD63 Extraction
Divisions:	Faculty of Natural Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Yolanda Tantri Selrizananta
Date Deposited:	05 Aug 2026 02:50
Last Modified:	05 Aug 2026 02:50
URI:	http://repository.its.ac.id/id/eprint/143839

Actions (login required)

View Item