Sintesis Dan Karakterisasi Zsm-5/G-C3n4 Berpori Sebagai Fotokatalis Pada Fotodegradasi Metilen Biru

Yuhaneka, Grace (2022) Sintesis Dan Karakterisasi Zsm-5/G-C3n4 Berpori Sebagai Fotokatalis Pada Fotodegradasi Metilen Biru. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 01211950012005-Master_Thesis.pdf Restricted to Repository staff only Download (3MB)

Abstract

Komposit ZSM-5/grafitik karbon nitrida (g-C3N4) berpori berhasil disintesis
dengan menggunakan metode solvothermal. Dengan memvariasikan jumlah
komponen ZSM-5 dan g-C3N4 berpori dalam komposit, peran masing-masing
komponen terhadap transfer pembawa muatan (elektron dan lubang positif), yang
berkontribusi pada peningkatan kinerja fotokatalitik, dapat dipelajari. Analisis XRD,
FTIR, SEM menunjukkan bahwa lebih banyak komponen ZSM-5 dalam komposit
menyebabkan interaksi yang lebih kuat dengan g-C3N4 berpori. Semakin banyak
jumlah ZSM-5 dalam komposit, semakin tinggi luas permukaannya. Uji kinerja
fotokatalitik terhadap degradasi metilen biru (MB) menunjukkan bahwa semakin
tinggi jumlah ZSM-5 juga menyebabkan aktivitas fokatalitik yang semakin baik. g
C3N4 berpori adalah komponen utama yang bertanggung jawab atas aktivitas
katalitik komposit karena sifat fotoaktifnya. Sementara itu, analisis spektroskopi
elektron impedansi (EIS) dan fotoluminesensi (PL) mengungkapkan peran ZSM-5,
yang dapat memfasilitasi transfer pembawa muatan dari g-C3N4 berpori ke
permukaan katalis karena konduktivitasnya yang lebih tinggi. Transfer pembawa
muatan yang difasilitasi oleh partikel ZSM-5 tersebut menekan rekombinasi
permukaan, sehingga meningkatkan kinerja katalitik komposit ZSM-5/g-C3N4
berpori dibandingkan dengan material g-C3N4 berpori.

----------------------------------------------------------

ZSM-5/porous graphitic carbon nitride (g-C3N4) composites were
successfully prepared using a simple solvothermal method. By varying the amount of
ZSM-5 and g-C3N4 component in the composites, the role of each component to the
charge carrier (electrons and holes) transfer, which contributes to the enhanced
photocatalytic performance, was unraveled. The XRD, FTIR, SEM analysis revealed
that more ZSM-5 component leads to more intact interaction with g-C3N4. The more
ZSM proportion in the composites, the higher surface area. Photocatalytic
performance test toward methylene blue (MB) degradation shows that the higher
protion of ZSM-5, the better phocatalytic activity. The porous g-C3N4 is the main
component responsible for the activity of the composites due to its photoactive
property.
Meanwhile, the impedance electron spectroscopy (EIS) and
photoluminescence (PL) analysis revealed the role of ZSM-5, which facilitates the
charge carrier transfers of photogenerated electrons and holes from g-C3N4 to the
catalyst surface due to its higher conductivity. The facilitated charge carrier transfer
by ZSM-5 particles suppressed the surface recombination, hence enhancing the
catalytic performance of the ZSM-5/g-C3N4 composites compared to bare g-C3N4.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	karbon nitrida, ZSM-5, fotokatalisis, fotodegradasi.
Subjects:	Q Science
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47101-(S2) Master Thesis
Depositing User:	magang .
Date Deposited:	31 Aug 2026 02:53
Last Modified:	31 Aug 2026 02:53
URI:	http://repository.its.ac.id/id/eprint/144425

Actions (login required)

View Item