Polimer Elektrolit Padat Nanokomposit Sio2/Peo/Naclo4 Untuk Baterai Na-Ion

Khoiriyah, Nuril (2022) Polimer Elektrolit Padat Nanokomposit Sio2/Peo/Naclo4 Untuk Baterai Na-Ion. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 01221750012001-Master_Thesis.pdf Restricted to Repository staff only Download (1MB)

Abstract

Polimer elektrolit padat dengan nilai konduktivitas yang tinggi telah
berhasil dibuat pada penelitian ini. Elektrolit merupakan salah satu komponen
utama baterai sebagai sarana penghantar elektron. Elektrolit jenis polimer padat
memiliki tingkat keamanan lebih tinggi daripada elektrolit jenis cairan. Polimer
elektrolit padat dari poli-etilen oksida (PEO) telah menunjukkan beberapa hasil
yang baik, akan tetapi masih membutuhkan beberapa modifikasi untuk lebih
meningkatkan nilai konduktivitasnya. Penambahan garam NaClO4 sebagai
pemlastis dan variasi persentase SiO2 dari sekam padi sebagai pengisi polimer
elektrolit dilakukan pada penelitian ini. Polimer elektrolit padat (PEP) yang
dihasilkan berbentuk bulat, pipih dan padat. Selanjutnya PEP dikarakterisasi
dengan XRD, FTIR, DSC dan EIS. Pola XRD menunjukkan adanya penurunan
kristalinitas pada PEP yang divariasi. Spektra FTIR menunjukkan adanya
interaksi ikatan Na+-PEO dan SiO2:ClO4-. Kondisi termal PEP optimum teramati
pada suhu antara 68° - 70°C dari termogram DSC. Hasil konduktivitas ionik
tertinggi yang diperoleh dari perhitungan impedansi EIS pada suhu 60°C yaitu
3,369×10−6 S/cm untuk PEP dengan penambahan SiO2 sebanyak 5% b/b. Nilai
konduktivitas ionik tersebut menunjukkan bahwa PEP merupakan elektrolit yang
menjanjikan untuk baterai Na-ion.

------------------------------------------------------------

A solid polymer electrolyte with a high conductivity value has been
successfully made in this study. Electrolyte is one of the main components of the
battery as a means of conducting electrons. Solid polymer electrolytes have a
higher safety level than liquid electrolytes. Solid polymer electrolyte of poly
ethylene oxide (PEO) has shown some good results, but still needs some
modifications to increase the conductivity value. The addition of NaClO4 salt as a
plasticizer and variations in the percentage of SiO2 from rice husk as a polymer
electrolyte filler were carried out in this study. The solid polymer electrolytes
(SPEs) produced are round, flat and solid. Furthermore, SPEs were characterized
by XRD, FTIR, DSC and EIS. The XRD pattern showed a decrease in the
crystallinity of the various SPEs. The FTIR spectra showed the interaction of Na+
PEO and SiO2:ClO4- bonds. Optimum SPE thermal conditions were observed at
temperatures between 68° - 70°C from the DSC thermogram. The highest ionic
conductivity obtained from the calculation of the EIS impedance at a temperature
of 60°C was 3.369×10−6 S/cm for SPE with the addition of 5% w/w of SiO2. This
ionic conductivity value shows that SPE is a promising electrolyte for Na-ion
batteries.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	solid-state polymer electrolyte, PEO, SiO2, Na-ion batteries.
Subjects:	T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2931 Fuel cells
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47101-(S2) Master Thesis
Depositing User:	magang .
Date Deposited:	31 Aug 2026 04:30
Last Modified:	31 Aug 2026 04:30
URI:	http://repository.its.ac.id/id/eprint/144426

Actions (login required)

View Item