Sintesis MCM-41 Menggunakan Sumber Silika dari Abu Layang Batubara Pt. Ipmomi Paiton dengan Variasi Komposisi dan Waktu Hidrotermal

Wiyanti, Dalia Novrinda (2010) Sintesis MCM-41 Menggunakan Sumber Silika dari Abu Layang Batubara Pt. Ipmomi Paiton dengan Variasi Komposisi dan Waktu Hidrotermal. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 1405100035-Undergraduate_thesis.pdf Restricted to Repository staff only Download (71MB)

Abstract

Penelitian ini diawali dengan proses leaching pada abu layang batubara, dilanjutkan dengan proses alkali fusi abu layang dengan NaOH. Sintesis MCM-41 menggunakan sumber silika dari hasil alkali fusi dilakukan dengan variasi komposisi yang menggunakan dua perbandingan mol gel, yakni CTAB:Si:H₂O adalah (A) 0,027:0,1:30 dan (B) 0,15:1:167 dan variasi waktu hidrotermal, yakni 96, 144, 192, dan 240 jam pada temperatur 100°C. Padatan hasil sintesis dikarakterisasi menggunakan XRD dan FTIR. Difraktogram menunjukkan puncak karakteristik pada 2θ sekitar 1,5–2,36°, 3,6–4,0°, 4,36–4,6°, dan 5,96–6,1° yang hampir sama dengan puncak karakteristik dari material MCM-41. Berdasarkan isoterm adsorpsi/desorpsi nitrogen diketahui bahwa padatan hasil sintesis memiliki luas permukaan spesifik 815,70–887,50 m²/g; dan diameter pori 34,03–34,06 Å. Hasil foto SEM menunjukkan bahwa padatan hasil sintesis merupakan kumpulan butiran-butiran partikel dengan morfologi seragam berdiameter kurang lebih 200 nm. Hasil pengukuran sifat keasaman menggunakan FTIR piridin menunjukkan bahwa MCM-41 hasil memiliki sisi asam Lewis dan sisi asam Brønsted karena adanya logam dalam kerangka MCM-41.
=====================================================================================================================================
This study was initiated by leaching process of coal fly ash, followed by alkali fused of coal fly ash with NaOH. Synthesis of MCM-41 using the result of alkali fused as silica source has been done in two different molar gel compositions, i.e. CTAB:Si:H₂O of (A) 0,027:0,1:30 and (B) 0,15:1:167 with variation of hydrothermal times, i.e. 96, 144, 192, and 240 hours at 100 °C. The results were investigated by XRD and FTIR. The diffractograms showed characteristic peaks at 2θ of 1,5–2,36°, 3,6–4,0°, 4,36–4,6°, and 5,96–6,1° which were similar to the characteristic peaks of MCM-41 materials. Nitrogen adsorption/desorption isotherms showed that the resulting MCM-41 have specific surface area of 815,70–887,50 m²/g and pore diameters of 34,03–34,06 Å. SEM images showed mainly agglomerations of equiaxed particles which have uniform morphology with diameters about 200 nm. The FTIR spectra of adsorbed pyridine showed that the resulting MCM-41 have Lewis and Brønsted acid sites which may be caused by incorporation of metal in framework of MCM-41.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	abu layang batubara, MCM-41, perbandingan mol gel, waktu hidrotermal,coal fly ash, MCM-41, comparation molar gel,hydrothermal time.
Subjects:	Q Science > QD Chemistry > QD481 Chemical structure.
Divisions:	Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	magang .
Date Deposited:	13 Oct 2026 04:23
Last Modified:	13 Oct 2026 04:23
URI:	http://repository.its.ac.id/id/eprint/145517

Actions (login required)

View Item