Polimerisasi Pirol, Tiofen, 3-Metiltiofen dan 3-Heksil Tiofen Secara Elektrokimia

Aryasa, I Wayan Tanjung (2009) Polimerisasi Pirol, Tiofen, 3-Metiltiofen dan 3-Heksil Tiofen Secara Elektrokimia. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 1405100062-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (9MB)

Abstract

Telah dilakukan penelitian mengenai polimerisasi secara kimia pada pirol, tiofen, 3-metiltiofen dan 3-heksiltiofen untuk mengatahui puncak-puncak oksidasinya. Elektropolimerisasi merupakan sebuah metode sederhana yang dapat digunakan untuk menghasilkan polimer konduktif. Keuntungan dari elektropolimerisasi yaitu polimer yang terbentuk siap didoping dan level doping dapat dikontrol. Polimerisasi secara kimia ini menggunakan metode voltametri siklik untuk mengetahui nilai puncak oksidasi monomer. Analisis voltametri siklik menunjukkan bahwa dengan variasi laju scan, dimana semakin lambat laju scan maka yang akan muncul puncak oksidasi saja sedangkan untuk laju scan yang lebih cepat maka yang muncul adalah puncak oksidasi dan puncak reduksinya. Voltametri siklik juga dapat menunjukkan perbedaan puncak oksidasi dari monomer pirol, tiofen, 3-metiltiofen dan 3-heksiltiofen, dimana nilai rata-ratanya sebesar 0,49V; 0,59V; 0,44V dan 0,65V, secara berurutan. Sedangkan puncak oksidasi untuk lapisan rangkap dimana lapisan dasarnya polipirol dan lapisan atasnya adalah monomer tiofen, 3-heksiltiofen dan 3-metiltiofen relatif berbeda, dengan nilai rata-ratanya adalah 0,8V; 1,3V dan 0,83V, secara berurutan. Mikroskop optik dapat digunakan untuk melihat adanya perbedaan yang jelas antara elektroda kerja yang dilapisi emas dengan elektroda kerja emas yang dielektropolimerisasi dengan monomer pirol, tiofen, 3-metiltiofen dan 3-heksiltiofen.
======================================================================================================================================
The polymerization of pyrrole, thiophene, 3-methylthiophene and 3-hexylthiophene by electrochemical method has been done. The advantages of the electropolimerization are the polymer was already doped and the dopping level of polymer can be controlled. The oxidation potentials of the monomer were determined by cyclic voltammetric methods. Cyclic voltammetric analysis with a variation of scan rate showed that at lower scan rate only oxidation peak was shown. At faster scan rate both oxidation and reduction peaks were appear. The oxidation of pyrrole, thiophene, 3-methylthiophene and 3-hexylthiophene was appear at different potential 0,49V; 0,59V; 0,44V and 0,65V, respectively. Even it: oxidation peaks for double layers with polypyrrole as based layer and thiophene, 3-hexylthiophene and 3-methylthiophene as top layer was relatively different, the averages oxidation values each monomer were 0,8V; 1,3V and 0,83V, respectively. Using optical microscope, there are clear different between gold working electrode and gold working electrode with polypyrrole, polythiophene, poly(3-methylthiophene) and poly(3-hexylthiophene).

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Elektropolimerisasi, Pirol, Tiofen, 3-Heksiltiofen, 3-Metiltiofen,Electropolimerization Pyrrole, Thiophene, 3-Hexylthiophene 3-Methylthiophene.
Subjects:	Q Science > QD Chemistry > QD481 Chemical structure.