Anggrianis, Riza (2011) Sintesis Geopolimer untuk Amobilisasi Logam Berat Pb. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 1406100050-Undergraduate_thesis.pdf Restricted to Repository staff only Download (56MB)

Abstract

Sintesis geopolimer dengan variasi rasio mol SiO2/Al2O3 dan perilaku amobilisasi geopolimer dengan kontaminan Pb(II) dalam bentuk garam nitrat telah dilakukan. Sintesis dilakukan dengan variasi mol SiO2/Al2O3 dengan penambahan Al(OH)3, dan perbandingan padat/cair yang digunakan 1,96. Kuat tekan tertinggi didapatkan pada rasio mol SiO2/Al2O3=3,75 yaitu 44,400x103 kN/m2 dan terendah pada SiO2/Al2O=2,50 yaitu 6,423x103 kN/m2. Perilaku amobilisasi logam berat diamati pada geopolimer dengan rasio mol SiO2/Al2O3=3,75 dan SiO2/Al2O3=2,50 dengan penambahan Pb(NO3)2. Efektivitas amobilisasi logam berat ini diuji dengan proses leaching dalam suasana asam menggunakan asam asetat pada pH ± 3 dan kekuatan amobilisasi ditentukan dari jumlah logam berat yang terleaching menggunakan ICP-OES. Studi perkembangan fasa dengan XRD menunjukkan bahwa pada rasio mol SiO2/Al2O3=3,75 mempunyai fasa amorf dengan quartz dan mullite sebagai mineral utamanya, sedangkan pada rasio mol SiO2/Al2O3=2,50 mineral utamanya berupa gibbsite. Studi morfologi dengan SEM menunjukkan bahwa struktur butiran terbentuk pada rasio mol SiO2/Al2O3=2,50, sedangkan struktur yang lebih homogen dan kompak terbentuk pada rasio mol SiO2/Al2O3=3,75. Logam berat Pb diamobilisasi dengan baik pada geopolimer dengan rasio mol SiO2/Al2O3=3,75 yang ditunjukkan dengan hasil leaching yang lebih sedikit.
=======================================================================================================================================
Synthesis of geopolymer by varying SiO2/Al2O3 mol ratio and immobilization behavior of geopolymer with contaminant Pb(II) in the form of nitrate salts have been carried out. Synthesis carried out using various SiO2/Al2O3 mol ratio with the addition of Al(OH)3, and the ratio of solid/liquid is 1,96. The highest compressive strength obtained at mol ratio of SiO2/Al2O3 = 3,75 was about 44,400 x 103 kN/m2 and the lowest at SiO2/Al2O3 = 2,50 mol ratio was about 6,423 x 10 kN/m. The behavior of heavy metal immobilization observed in geopolymer with SiO2/Al2O3 = 3,75 mole ratio and SiO2/Al2O3 = 2,50 with the addition of Pb(NO3)2. The effectiveness of immobilization of heavy metals was tested with leaching process under acid condition with acetic acid at pH ± 3 and immobilization strength determined from the amount of heavy metals in leachate solution will be determined by ICP-OES. Phase development study by XRD showed that the mole ratio SiO2/Al2O3 = 3,75 have amorphous phase with quartz and mullite as major minerals, whereas the mole ratio of SiO2/Al2O3 = 2,50 has main gibbsite mineral. Morphological studies by SEM showed that the granules structure formed on SiO2/Al2O3 = 2,50 mol ratio, while the structure is more homogeneous and compact form on SiO2/Al2O3 = 3,75 mol ratio. Heavy metal Pb was immobilized by both the geopolymer with SiO2/Al2O3 mole ratio = 3.75 as indicated by the results of leaching fewer.

Item Type:	Thesis (Other)
Additional Information:	RSKi 547.7 Ang s
Uncontrolled Keywords:	Logam Berat, Geopolimer, Amobilisasi, Leaching, Heavy Metal, Geopolymer, Immobilization, Leaching
Subjects:	Q Science > QD Chemistry > QD481 Chemical structure.
Divisions:	Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	magang .
Date Deposited:	16 Oct 2026 07:31
Last Modified:	16 Oct 2026 07:31
URI:	http://repository.its.ac.id/id/eprint/145652

Actions (login required)

View Item