PRASETYA, DONY (2017) ANALISIS PENGARUH VARIASI WAKTU TAHAN DAN TEMPERATUR TEMPERING TERHADAP SIFAT KEKERASAN MATERIAL CROSSBAR YANG DI HARDENING SEBAGAI SOLUSI KEGAGALAN PADA CROSSBAR. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2713100093-Undergraduate_Theses.pdf - Published Version Download (6MB) | Preview |
Abstract
Clinker cooler adalah alat yang berfungsi mentrasportasikan clinker menuju hammer crusher. Salah satu bagian dari clinker cooler adalah crossbar. Crossbar sering mengalami crack sehingga mengurangi umur pakai dari clinker cooler. Dalam penelitian ini, dilakukan analisis kegagalan dari crossbar dan solusi dari kegagalan tersebut berupa hardening dan tempering. Pengujian yang dilakukan untuk menganalisis material ini adalah uji komposisi, uji streomikroskop, uji SEM, metalografi, dan uji kekerasan Berdasarkan pengujian OES dan kekerasan, faktor yang kegagalan adalah kesalahan dalam pemilihan material yang ditinjau dari komposisi material, kekerasan material. Solusi dari kegagalan ini yaitu perlakuan panas yang dapat menghasilkan kekerasan yang sesuai dengan standar kekerasan ASTM A48 adalah hardening dan tempering 300oC dengan waktu tahan 120 menit, hardening dan tempering 350oC dengan waktu tahan 120 menit, hardening dan tempering 400oC dengan waktu tahan 120 menit, dan hardening dan tempering 300oC dengan waktu tahan 60 menit. ==============================================================================
Clinker cooler is an equipment that has function to move clinker to hammer crusher. One of the clinker cooler’s part is crossbar. Crossbar often have a failure in form of crack and decrease the lifetime of clinker cooler. This study content of failure analysis and how to solve the failure by hardening and tempering. To analize the failure, researcher do some examination such as element content analysis, stereomicroscope observation, SEM, metallography, dan hardness test. According to element content analysis and hardness test, cause of the failure is wrong material selection based on content of the material and the hardness of material. The solution of the failure is heat treatment that can hardened the material according to the hardness standard ASTM A48. The type of heat treatments are hardening and tempering 300oC with holding time 120 minutes, hardening and tempering 350oC with holding time 120 minutes, hardening and tempering 400oC with holding time 120 minutes, dan hardening dan tempering 300oC with holding time 60 minutes.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Crossbar, Crack, Hardening, Tempering, ASTM A48 |
| Subjects: | T Technology > TN Mining engineering. Metallurgy |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | DONY PRASETYA - |
| Date Deposited: | 27 Feb 2017 03:27 |
| Last Modified: | 05 Mar 2019 03:13 |
| URI: | http://repository.its.ac.id/id/eprint/1642 |
Actions (login required)
 |
View Item |