Pengaruh Penambahan Montmorillonite Pada Sifat Ketahanan Termal Polivinil Asetat

Hanafi, Muchammad Izzuddin Jundullah (2016) Pengaruh Penambahan Montmorillonite Pada Sifat Ketahanan Termal Polivinil Asetat. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1412100050-Undergraduate-Thesis.pdf]
Preview
Text
1412100050-Undergraduate-Thesis.pdf - Published Version

Download (1MB) | Preview

Abstract

Polimerisasi emulsi PVAc dari PVA dan VAM menggunakan metode semibatch telah dipelajari. PVAc disintesis menggunakan pelarut DMSO dengan variasi penambahan montmorillonite 1%, 2%, dan 3%. Hasil analisis menggunakan spektroskopi FTIR menunjukkan adanya kemiripan gugus fungsi antara PVAc solvent based dengan PVAc hasil sintesis. Karakterisasi menggunakan Thermogravimetric Analysis (TGA) menunjukkan PVAc solvent based memiliki dekomposisi termal lebih baik dibandingkan PVAc hasil sintesis, yaitu 76,16% pada suhu 280-380°C dan 22,37% pada suhu 400-500°C.
==================================================================================================================
PVAc emulsion polymerizations from PVA and VAM through semibatch method have been studied. The polymerization used DMSO as solvent with montmorillonite filler of 1%, 2%, and 3% addition. The results of analysis using FTIR spectorcopy show that industrial, solvent based PVAc has similar functional group with the PVAc synthesized. Thermogravimetric Analysis (TGA) characterization shows that industrial, solvent based PVAc has the best thermal decomposition than the other PVAc synthesized, which is 76,16% at temperature of 280-380°C and 22,37% at temperature of 400-500°C.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 622.79 Han p
Uncontrolled Keywords: Monomer Vinil Asetat, Polivinil Alkohol, Montmorillonite
Subjects: Q Science > QD Chemistry > Polymerization
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Users 13 not found.
Date Deposited: 19 Jun 2017 07:18
Last Modified: 26 Dec 2018 08:41
URI: http://repository.its.ac.id/id/eprint/41747

Actions (login required)

View Item View Item