Banjarnahor, Orlando (2017) Studi Pengaruh Variasi Perbandingan Rasio Massa Naoh Dengan Calcinaced Petroleum Coke (CPC) Terhadap Derajat Desulfurisasi CPC Menggunakan Reaktor Rotary Autoclave. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2713100074-Undergraduate_Thesis.pdf - Published Version Download (4MB) | Preview |
Abstract
Industri pengolahan minyak bumi mentah dapat menghasilkan produk sampingan yang masih bias digunakan untuk keperluan industri lainnya. Salah satu produk sampingan itu adalah petroleum coke (kokas). Salah satu jenis petroleum coke adalah CPC (Calcined Petroleum Coke) yang biasa digunakan sebagai bahan dasar pembuatan anoda dalam industri pemurnian aluminium. Adapun masalah calcined petroleum coke hingga saat ini adalah keberadaan unsur sulfur (S) di dalamnya yang dapat membentuk senyawa SO2/SO3 yang berbahaya bagi lingkungan. Proses desulfurisasi calcined petroleum coke adalah salah satu proses yang diharapkan dapat menekan keberadaan sulfur serendah-rendahnya pada calcined petroleum coke agar dapat digunakan. Proses pengurangan kadar sulfur pada CPC dapat dilakukan dengan proses desulfurisasi termal dengan senyawal alkali NaOH padat menggunakan reaktor rotary autoclave. Dimana variasi rasio massa yang digunakan dalam penelitian ini, yaitu rasio massa CPC terhadap NaOH antara lain 1:0.5 ; 1:1 ; 1:1.5. Adapun tujuan dari penelitian ini adalah untuk menganalisa pengaruh variasi rasio massa NaOH terhadap kadar sulfur dan karbon dalam CPC dan terhadap ikatan molekul dalam CPC. Dari proses penelitian diperoleh hasil bahwa penurunan derajat desulfurisasi pada CPC paling tinggi diperoleh saat perbandingan massa CPC dengan NaOH adalah 1;1.5, dimana derajat desulfurisasinya adalah 70.1%. Sedangkan derajat desulfurisasi yang paling rendah terdapat pada perbandingan 1:0.5 yaitu sebesar 61%. Dan pada perbandingan 1:1 derajat desulfurisasinya sebesar 62.3%.
========================================================================================================================
The crude petroleum processing industry can produce byproducts that can still be used for other industrial purposes. One of the byproducts is petroleum coke (coke). One type of petroleum coke is the CPC (Calcined Petroleum Coke) commonly used as an anode manufacturing base in the aluminum refining industry. The problem of calcined petroleum coke to date is the presence of sulfur (S) elements in it that can form SO2 / SO3 compounds that are harmful to the environment. The calcined petroleum coke desulfurization process is one of the processes which is expected to suppress the presence of sulfur as low as possible in calcined petroleum coke to be used. The process of reducing sulfur content in CPC can be done by thermal desulfurization process with alkali solid NaOH compound using rotary autoclave reactor. Where variation of mass ratio used in this research, that is ratio of mass of CPC to NaOH among others 1:0.5 ; 1:1 ; 1:1.5. The purpose of this research is to analyze the effect of variation of NaOH mass ratio to sulfur and carbon content in CPC and to molecular bond in CPC.From the research process, it was found that the desulfurization increase in the highest CPC was obtained when the ratio of CPC mass to NaOH was 1:1.5, where the desulfurization degree was 70.1%. While the lowest degrees of desulfurization is in the 1:0.5 ratio of 61.0%. And at a ratio of 1:1 degrees of desulfurisation of 62.3%.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Calcinaced Petroleum Coke, desulfurization, mass ratio, solid NaOH, sulphur |
| Subjects: | T Technology > TN Mining engineering. Metallurgy |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Orlando Banjarnahor . |
| Date Deposited: | 25 Aug 2017 08:03 |
| Last Modified: | 05 Mar 2019 04:47 |
| URI: | http://repository.its.ac.id/id/eprint/43091 |
Actions (login required)
 |
View Item |