Julianto, Henry (2017) Pengembangan Bahan Akustik dan Insulasi Termal Berbasis Komposit Silicone Rubber Berpenguat Nanoselulosa Dari Serat Tandan Kosong Kelapa Sawit Untuk Muffler. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2713100090_Undergraduate_Theses.pdf - Published Version Download (7MB) | Preview |
Abstract
Kebisingan merupakan polusi suara yang berdampak negatif terlebih disektor transportasi. Banyak kendaraan bermotor yang mana kendaraan jenis ini menimbulkan kebisingan yang cukup tinggi (>80db) dan dapat mengganggu aktivitas manusia. Terlebih banyak manusia yang kakinya terluka dikarenakan terkena panas dari knalpot bagian luar. Tujuan dari penelitian ini adalah menganalisis pengaruh fraksi berat terhadap morfologi, nilai koefisien absorpsi suara, densitas, stabilitas termal, dan konduktivitas termal. Bahan komposit berpenguat STKKS merupakan sebuah alternatif material peredam akustik dan insulasi panas yang ramah lingkungan. Pada penelitian ini dibuat komposit berpenguat serat tandan kosong kelapa sawit dengan matriks silicone rubber berpori. Variabel yang digunakan pada penelitian ini adalah pengaruh fraksi berat nanoselulosa (0, 6 dan 8%). Pengujian yang dilakukan dalam penelitian ini meliputi koefisien absorpsi suara, SEM, TEM, TGA, FTIR, densitas, dan konduktivitas termal. Penambahan fraksi berat menyebabkan perubahan jumlah dan bentuk pori. Pori teratur dengan jumlah besar ada pada silicone rubber/nanoselulosa 6% dengan 27.366% area. Nilai α tertinggi pada frekuensi 4000 Hz ada pada pada silicone rubber/nanoselulosa 6%, yaitu sebesar 0,4358. Penambahan fraksi berat juga menyebabkan perubahan konduktivitas termal dengan tujuan sebagai material insulasi. Penambahan fraksi berat nanoselulosa dalam komposit membuat konduktivitas termal semakin kecil dimana material tersebut semakin baik sebagai penginsulasi panas tetapi memiliki stabilitas termal yang rendah seiring penambahan serat. Dalam hal insulasi, Silicone rubber berpori/nanoselulosa 8% merupakan yang paling baik dengan konduktivitas sebesar 0.19891 W/moC. Sedangkan dalam hal stabilitas termal, Silicone rubber berpori murni memiliki kestabilan termal yang paling baik karena penambahan nanoselulosa mengurangi stabilitas termal
===============================================================================================
Loudness or noise is a sound pollution that has a negative impact in the transportation sector. There is many motor vehicles generate a high noise ( about > 80 dB) and can interfere with human activity. More people whose legs are hurt due to exposure to heat from the exhaust outside. The purpose of this research is to analyze the influence of nanocellulose fraction to morphology, sound absorption coefficient, density, thermal stability, and thermal conductivity. The OPEFB (Oil Palm Empty Fruit Bunch) composite material is an alternative to environmentally friendly acoustic damper and heat insulation. In this research, composites were made of OPEFB with porous silicone rubber matrix. The variable used in this research is the influence of nanocellulose weight fraction (0, 6 and 8%). Tests conducted in this research include sound absorption coefficient, SEM, TEM, TGA, FTIR, density, and thermal conductivity. The addition of the weight fraction causes changes in the amount and shape of the pore. Pore with large amounts are present on 6% silicone rubber / nanocellulose with 27.366% area. The highest value of α at 4000 Hz is in silicone rubber / nanocellulose 6%, which is 0.4358. The addition of the weight fraction of nanocellulose also causes a change in thermal conductivity with the purpose of being an insulating material. The addition of fractions of nanoselulose in the composite makes the thermal conductivity smaller when the material is better as heat insulator but has a low thermal stability as the addition of fiber. In the case of insulation, silicone rubber/nanocellulose 8% is the best with a conductivity of 0.19891 W / moC. While in terms of thermal stability, pure porous silicon rubber has the best thermal stability because the addition of nanocellulose reduces thermal stability
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Muffler, Thermal Stability, Thermal Conductivity, Silicone Rubber, Blending |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials. T Technology > TD Environmental technology. Sanitary engineering > TD892 Noise control T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles. |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Henry .Julianto |
| Date Deposited: | 20 Sep 2017 02:02 |
| Last Modified: | 01 Mar 2019 07:53 |
| URI: | http://repository.its.ac.id/id/eprint/43214 |
Actions (login required)
 |
View Item |