Iqbal, Muhammad Naufal (2017) Analisa Pengaruh Temperatur Fluida Dan Lapisan Rubber Coating Terhadap Karakteristik Korosi Pada Pipa Baja Karbon Yang Terinsulasi Bahan Glasswool Dan Aluminium Foil. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2713100141-Undergraduate-Theses.pdf - Published Version Download (1MB) | Preview |
Abstract
Korosi dibawah insulasi merupakan masalah serius bagi dunia industri yang menggunakan pipa terinsulasi untuk mengalirkan fluida panas atau dingin. Korosi dibawah insulasi ini sulit dideteksi karena korosi yang terjadi pada permukaan luar pipa terbungkus bahan insulasi. Dalam penelitian kali ini dicari bagaimana karakteristik korosi yang terjadi pada permukaan pipa yang terinsulasi. Penelitian ini memodelkan bagaimana suatu pipa terinsulasi bekerja pada proses sebenarnya. Pipa yang digunakan adalah pipa baja karbon dan bahan insulasi yang dipakai adalah glasswool dan aluminium foil. Variable yang digunakan adalah temperatur fluida dalam pipa yaitu 45, 55, 65, dan 75oC. Sedangkan variasi lapisan coating yang digunakan yaitu tanpa coating dan dengan pelapisan coating. Jenis lapisan coating yang digunakan adalah cat berbasis rubber dengan coating primer akrilik. Pengujian dilakukan selama empat belas hari agar tercipta korosi pada pipa. Setelah periode pengujian, pipa tersebut di analisa karakteristik korosinya. Hasil pengujian weightloss pada pipa coating dan non-coating menunjukan peningkatan laju korosi seiring peningkatan temperatur. Sementara hasil pengujian XRD menunjukan bahwa produk korosi yang terbentuk adalah senyawa Fe2O3, sedangkan hasil pengujian mikroskop optik dan SEM menunjukan bahwa jenis korosi yang timbul pada permukaan pipa merupakan uniform corrosion. =====================================================================
Corrosion under insulation is a serious problem for the industry who using insulated pipes to drain hot or cold fluids. Corrosion under this insulation is difficult to detect because the corrosion that occurs on the outer surface of the pipe is wrapped by insulating material. In this research study sought how the corrosion characteristics that occur on the surface of the insulated pipe. This research modeled how an insulated pipe works on the actual process. The pipe which used is carbon steel pipe and the insulation material used is glasswool and aluminum foil. The variables used are fluid temperature in pipes that is 45, 55, 65, and 75oC. While the coating layer variation used is pipe without coating and pipe with coating. Type of coating layer used is rubber-based paint with acrylic primer coating. The test was conducted for fourteen days to create corrosion of the pipe. After the test period, the pipe is analyzed for its corrosion characteristics. The results of weightloss testing on coating and non-coating pipes show an increase in corrosion rate as temperature increases. While XRD test results show that the corrosion products formed are Fe2O3, while the results of optical microscopy and SEM testing show that the type of corrosion that arises on the surface of the pipe is a uniform corrosion.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Korosi dibawah Insulasi, Glasswool, Rubber Coating, SEM, XRD, Weightloss, Mikroskop Optik, Corrosion under Insulation, Optical Microscope. |
| Subjects: | Q Science > QD Chemistry > QD502 Chemical kinetics T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Muhammad Naufal Iqbal |
| Date Deposited: | 25 Sep 2017 08:20 |
| Last Modified: | 06 Mar 2019 03:25 |
| URI: | http://repository.its.ac.id/id/eprint/43957 |
Actions (login required)
 |
View Item |