Fatkhurohmat, Heru (2017) Aplikasi Ekstrak Kulit Jeruk Nipis (Citrus Aurantifolia) Sebagai Inhibitor Organik Pada Baja Api 5L Grade B Media Larutan H2SO4 1M. Diploma thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2114030104-Non_Degree.pdf - Published Version Download (8MB) | Preview |
Abstract
Korosi yang terjadi pada logam telah menimbulkan permasalahan yang serius di berbagai bidang seperti halnya pada industri dan konstruksi termasuk industri minyak dan gas. Korosi tidak dapat dihindari atau dihilangkan, namun dapat dikendalikan. Salah satu upaya yang dapat digunakan untuk mengendalikan korosi pada logam karena pengaruh lingkungan yaitu dengan menambahkan inhibitor. Inhibitor organik merupakan suatu inhibitor yang berasal dari bahan alami seperti ekstrak sayur, dedaunan ataupun buah. Salah satunya yang dapat digunakan untuk inhibitor organik yaitu kulit jeruk nipis. Penelitian ini dilakukan dengan tujuan untuk mengetahui pengaruh inhibitor kulit jeruk nipis terhadap laju korosi yang terjadi pada baja API 5L grade B dengan media larutan H2SO4 1M. Pembuatan ekstrak dengan menggunakan metode maserasi. Konsentrasi inhibitor yang digunakan adalah 0 mg – 250 mg (kelipatan 50 mg). Pengujian yang dilakukan pada sampel uji yaitu Polarisasi, EIS, weight loss, FTIR dan SEM. Pada konsentrasi 200 mg menghasilkan efisiensi tertinggi di pengujian polarisasi sebesar 99.238% dan pengujian EIS sebesar 99.050%. Pengujian FTIR menunjukkan adanya gugus fungsi yang teradsorpsi pada permukaan baja API 5L grade B. Hasil SEM menunjukkan adanya lapisan tipis yang terbentuk, diduga lapisan ini yang membantu proses penghambatan laju korosi yang sedang terjadi pada spesimen.
=================================================================
Corrosion that occurs on metal has caused serious problems in various fields as well in industry and construction including the oil and gas industry. Corrosion cannot be avoided or removed, but can be controlled. One effort that can be used to control corrosion on metal because of the influence of the environment that is by adding an inhibitor. Organic inhibitors is inhibitor derived from natural ingredients such as vegetable extract, foliage or fruit. One of them that can be used for organic inhibitor that is peel lime. This research was conducted with the aim to find out the influence of peel lime (citrus aurantifolia) inhibitor against the corrosion rate of the steel API 5L grade B with H2SO4 1M solution. Making of the extract by using method of maceration. The concentration of inhibitor that is used is 0 mg – 250 mg (multiples of 50 mg). Research conducted on a sample test that is polarization, EIS, weight loss, FTIR and SEM. At concentration of 200 mg of the highest efficiency in a result of polarization is 99.238% and EIS result is 99.050%. FTIR result shows the functional groups that adsorption on the surface of the steel API 5L grade B. SEM result shows that there is a thin layer that is formed, supposedly this layer helps the process of the inhibition of the corrosion rate on a specimen.
| Item Type: | Thesis (Diploma) |
|---|---|
| Uncontrolled Keywords: | Korosi, Inhibitor Organik, Kulit Jeruk Nipis, Corrosion, Inhibitor Organic, Peel Lime, Steel API 5L, H2SO4 |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives |
| Divisions: | Faculty of Vocational > Mechanical Industrial Engineering (D4) |
| Depositing User: | Heru Fatkhurohmat . |
| Date Deposited: | 22 Nov 2017 02:24 |
| Last Modified: | 06 Mar 2019 06:58 |
| URI: | http://repository.its.ac.id/id/eprint/44098 |
Actions (login required)
 |
View Item |