Nurhadi, Bedry (2017) Perancangan Sistem Proteksi Katodik Arus Paksa pada Pipa Baja API 5L Grade B dengan Variasi Geometri dan Luas Permukaan Anoda di Dalam Tanah. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2713100133-undergraduate_thesis.pdf - Published Version Download (6MB) | Preview |
Abstract
Korosi adalah penurunan mutu logam akibat reaksi elektro kimia dengan lingkungannya Proses perkaratan termasuk proses elektrokimia, di mana logam Fe yang teroksidasi bertindak sebagai anode dan oksigen yang terlarut dalam air yang ada pada permukaan besi bertindak sebagai katode. Proteksi katodik merupakan salah satu cara yang digunakan banyak orang dalam pengendalian korosi, salah satu metode yang digunakan adalah metode Impressed Current Cathodic Protection (ICCP) yang menggunakan arus balik untuk menahan laju korosi. Penelitian ini menggunakan metode ICCP. Bahan penelitian berupa katoda berupa spesimen baja API 5L Grade B dan anoda grafit. Variabel yang digunakan dalam penelitian ada dua, yang pertama adalah coating dua lapis dan tanpa coating dan yang kedua adalah variasi geometri anoda yaitu bentuk silinder panjang, bentuk silinder pendek, dan bentuk kubus. Pipa memiliki panjang sebesar 1.5 m, dengan lebar diameter 0.0508 m sementara anoda memiliki luas permukaan yang berbda masing-masing 142 cm2, 132 cm2, dan 162 cm2. Pengukuran saat penelitian adalah pengukuran arus proteksi dan tegangan proteksi, serta pengukuran pH dan resistivitas tanah untuk mengetahui faktor lain yang dapat mempengaruhi sistem ICCP. Pipa yang diberikan perlakuan coating cenderung memerlukan arus proteksi yang lebih kecil disbanding dengan pipa tanpa coating yaitu sebesar 18-22 mA. Sementara itu, anoda yang memiliki luas permukaan yang besar, cenderung dapat mengeluarkan arus keluaran maksimum yang besar pula seperti anoda C yang memerlukan kebutuhan arus proteksi hanya 6 mA
=================================================================================================
Corrosion is the degradation of metal quality due to electrochemical reactions to the environment. The process of carnation includes the electrochemical process, Fe metals act as anode and oxygen dissolved in water present on the iron surface acts as a cathode. Cathodic protection is one way that many people use in corrosion control, one of the methods used is Impressed Current Cathodic Protection (ICCP) method that uses backflow to withstand the rate of corrosion. This research uses ICCP method. Research materials are API 5L pipesteel as cathode and graphite anode. There were two variables that used, the first is coating two layers and without coating and the second is anode geometry variation of the long cylinder shape, short cylinder shape, and cube shape. The pipe has a length of 1.5 m, with a diameter width of 0.0508 m while the anode has a respective surface area of 142 cm2, 132 cm2, and 162 cm2. The measurement that is needed were of protection current and protection voltage, and pH and soil resistivity measurements to determine other factors that may affect ICCP system. The pipe provided by the coating treatment tends to require a smaller protection current than the uncoated pipe 18-22 mA. Meanwhile, the anode having a large surface area, tends to output a large maximum output current as well as anode C which requires a current protection current of only 6 mA
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSMt 620.137 Nur p-1 |
| Uncontrolled Keywords: | Korosi, Proteksi Katodik, Arus Paksa, Pipa API 5L, Anoda Grafit, Geometri, Luas Permukaan |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Bedry Nurhadi |
| Date Deposited: | 17 Nov 2017 08:03 |
| Last Modified: | 06 Mar 2019 04:30 |
| URI: | http://repository.its.ac.id/id/eprint/44135 |
Actions (login required)
 |
View Item |