Analisis Pengaruh Variasi Kecepatan Aliran Gas Pelindung Hasil Pengelasan GMAW Terhadap Kekuatan Mekanik Dan Struktur Mikro Alumunium Seri 5083

Firmansyah, Dicky Rizki (2017) Analisis Pengaruh Variasi Kecepatan Aliran Gas Pelindung Hasil Pengelasan GMAW Terhadap Kekuatan Mekanik Dan Struktur Mikro Alumunium Seri 5083. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 4313100044-Undergraduate-Theses.pdf]
Preview
Text
4313100044-Undergraduate-Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Alumunium 5083 kerap digunakan atau diaplikasikan penggunaannya untuk vessels hull, bodies of aircarft, rail road karena paduan alumunium ini memiliki sifat yang ringan, memiliki daya resistensi yang baik terhadap korosi juga memiliki ductility yang bagus. Tujuan penelitian ini untuk mengetahui dan mendapatkan pengaruh dari variasi kecepatan aliran gas pelindung terhadap kekuatan tarik, kekerasan dan pengamatan struktur mikro Alumunium seri 5083. Adapun variasi kecepatan aliran gas pelindung yang digunakan adalah 20, 25 dan 30 liter/menit dengan elektroda ER5356. Hasil pengamatan struktur mikro menunjukan bahwa pengelasan menggunakan argon menghasilkan butir-butir kecil dan diketahui adanya pembentukan formasi Mg2Si. Seiring dengan peningkatan laju aliran gas akan meningkatkan bentuk butir-butir kecil dan pembentukan adanya Mg2Si yang dapat meningkatkan kekuatan tarik dan kekerasan. Dari hasil pengujian tarik didapatkan kecepatan aliran gas pelindung 25 liter/menit mempunyai nilai yield strength tertinggi yaitu 182,50 MPa dan ultimate strength 247,06 MPa sedangkan pada hasil pengujian kekerasan didapatkan nilai kekerasan tertinggi ketika variasi kecepatan aliran gas 30 liter/menit dengan nilai kekerasan pada Base Metal 79,01 HVN, HAZ 78,72 HVN dan Weld Metal 68,22.
=================================================================
Aluminum 5083 is often used or applied for hull vessels, bodies of aircarft, rail road because aluminum alloy has a lightweight properties, good resistance to corrosion resistance also good ductility. The purpose of this research is to know and to get influence from variation of shielding gas flow rate to tensile strength, hardness and observation of Alumunium 5083 series microstructure. The variation of shielding gas flow rate used is 20, 25 and 30 liter/min with ER5356 electrode. The result of micro structure observation shows that welding using argon produces small grains and the formation of Mg2Si is known. Along with the increase in gas flow rate will increase the form of small grains and the formation of Mg2Si which can increase tensile strength and hardness. From the tensile test results obtained shielding gas flow of 25 liters/minute has the highest yield strength value 182.50 MPa and ultimate strength 247.06 MPa whereas the hardness test results obtained the highest hardness value when variations gas flow rate of 30 liters/Minute with hardness value on Base Metal 79.01 HVN, HAZ 78.72 HVN and Weld Metal 68.22.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Alumunium 5083, vessels hull, Gas Metal Arc Welding.
Subjects: T Technology > TN Mining engineering. Metallurgy
V Naval Science > VM Naval architecture. Shipbuilding. Marine engineering
Divisions: Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User: Firmansyah Dicky Rizki
Date Deposited: 27 Nov 2017 04:04
Last Modified: 08 Mar 2019 03:59
URI: http://repository.its.ac.id/id/eprint/45678