Putra, Adams Pranantha Cahya (2017) Analisa Rekondisi Baja Pegas Daun Bekas SUP 9A Dengan Metode Quench-Temper Pada Temperatur Tempering 500 C Terhadap Kekerasan Dan Kekuatan Tarik. Diploma thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2114030066-Non_Degree.pdf - Published Version Download (8MB) | Preview |
Abstract
Kenyamanan dan keamanan saat berkendara menjadi hal yang sangat penting. Salah satu komponen untuk membuat aman dan nyaman saat berkendara ialah pada sistem suspensinya atau pegas daun. Pegas daun yang telah digunakan akan mengalami penuruan kualitas sifat mekanik yang dikarenakan beban dinamis yang diterima. Oleh karena itu, perlu dilakukan proses rekondisi untuk mengembalikan sifat mekanik sesuai standart spesifikasi awal baja pegas daun JIS G 4801-1984. Metodologi pada penelitian ini dilakukan dengan uji laku panas dengan proses pemanasan pada temperatur 850 C dengan holding time 60 menit, dilakukan proses quenching menggunakan media pendinginan air bervolume 20 Liter dengan cara agitasi, dilakukan proses Tempering pada temperatur 500 C dengan holding time 90 menit dan didinginkan dengan media udara, kemudian dilakukan uji tarik dan uji kekerasan. Dari hasil pengujian diperoleh baja pegas rekondisi tidak dapat mengembalikan kualitas sifat mekanik dan tidak memenuhi standar spesifikasi awal baja pegas daun JIS G 4801-1984. Kekuatan tarik (ultimate strength) yang dihasilkan sebesar 1140,90 MPa, kekuatan luluh (yield strength) sebesar 883,79 MPa, serta kekerasan sebesar 42,74 HRC atau 398,05 HB.
=========================================================================================
Safety and comfort become the most important factor
while driving. One way to provide more comfort and safety while
driving is managing the vehicle suspension system or leaf spring.
Leaf springs that have been used will have a decrease in the
quality of mechanical properties due to dynamic loads received.
Therefore, a recondition process is necessary to restore
mechanical properties to the standard specification leaf spring
JIS G 4801-1984
Methods in this research begin heat treatment at 850 ᵒC
with 60 minutes holding time and quenching cooled using 20
liters of water by means of agitation, then tempering process is
done at 500 ᵒC with 90 minutes holding time and cooled by air,
lastly hardness and tensile tests.
From the test result obtained that reconditioned spring
steel can not restore the quality of mechanical properties and
does not meet the standard specification of JIS G 4801 – 1984.
Ultimate tensile strength of 1140,90 Mpa, yield strength of 883,79
Mpa and also hardness of 42,74 HRC or 398,05 HB.
| Item Type: | Thesis (Diploma) |
|---|---|
| Uncontrolled Keywords: | Rekondisi, Pegas Daun, Quenching, Tempering, Sifat Mekanik. |
| Subjects: | T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment T Technology > TS Manufactures > TS156 Quality Control. QFD. Taguchi methods (Quality control) |
| Divisions: | Faculty of Vocational > Mechanical Industrial Engineering |
| Depositing User: | Adams Pranantha Cahya Putra |
| Date Deposited: | 26 Oct 2017 05:59 |
| Last Modified: | 05 Mar 2019 08:29 |
| URI: | http://repository.its.ac.id/id/eprint/47516 |