Pengaruh Variasi Rasio mol Na2O/SiO2 pada pembentukan Zeolit Y dari Kaolin melalui tahap Metakaolinisasi

Rizaldi, Nabil Ahmad (2017) Pengaruh Variasi Rasio mol Na2O/SiO2 pada pembentukan Zeolit Y dari Kaolin melalui tahap Metakaolinisasi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1413100109_Undergraduate Theses.pdf]
Preview
Text
1413100109_Undergraduate Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Penelitian ini bertujuan untuk mengetahui pengaruh variasi rasio mol Na2O/SiO2 terhadap sintesis zeolit Y melalui tahap metakaolinisasi. Sintesis zeolit Y dilakukan dengan metakaolin sebagai prekursor diikuti dengan komposisi variasi rasio mol Na2O/SiO2 4-10 Na2O : Al2O3 : 10 SiO2 : 180 H2O melalui proses pemeraman dan hidrotermal selama 24 jam pada suhu 100℃. Padatan hasil sintesis dikarakterisasi menggunakan difraksi sinar-X (XRD), spektroskopi inframerah (FTIR) dan Scanning Electron Microscopy Energy Dispersive X-Ray (SEM-EDX). Hasil karakterisasi dengan XRD dan spektroskopi inframerah menunjukkan fase zeolit Y terbentuk pada variasi rasio mol Na2O/SiO2 = 6 dan 8. Pada variasi rasio mol Na2O/SiO2 = 10 terbentuk fase sodalit. Hasil SEM-EDX menunjukkan morfologi hasil sintesis pada variasi rasio mol Na2O/SiO2 = 6 dan 8 menyerupai bentuk oktahedral dengan perbandingan rasio SiO2/Al2O3 sebesar 2,36; 2,78 dan 3,92.

==================================================================================

The purpose of this research was studied the effect of variation Na2O/SiO2 mol ratio towards synthesis zeolite Y through metakaolinization. Synthesis of zeolite Y was done by metakaolin as precursor and variation of the mol ratio 4-10 Na2O : Al2O3 : 10 SiO2 : 180 H2O following by aging and hydrothermal process for 24 hours at 100℃. Solid products were characterized using infrared spectroscopy (FTIR), X-ray diffraction (XRD), Scanning Electron Microscopy-Energy Dispersive X-ray (SEM-EDX). The result of XRD difractometer showed zeolite Y was formed at Na2O/SiO2 = 6 and 8 mol ratio. Sodalit phase was formed on variation Na2O/SiO2 = 10 mol ratio. SEM micrograf showed that mol variation ratio Na2O/SiO2 = 6 and 8 approach octahedral form with ratio SiO2/Al2O3 2,36; 2,78 and 3,92.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Sodalit, Zeolit Y, variasi rasio mol Na2O/SiO2, metakaolin
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Nabil Ahmad Rizaldi
Date Deposited: 06 Nov 2017 07:37
Last Modified: 05 Mar 2019 06:34
URI: http://repository.its.ac.id/id/eprint/48224

Actions (login required)

View Item View Item