Al Bisthomi, Moch. Khabibi (2017) Efek Minyak Tumbuhan Terhadap Sifat Mekanik Dan Termal Poliester Tak-Jenuh/Minyak Tumbuhan Sebagai Resin Biopolimer Yang Ramah Lingkungan. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2710100022-Undergraduate_Theses.pdf - Accepted Version Download (2MB) | Preview |
Abstract
Poliester adalah jenis polimer thermoset yang terbuat dari reaksi polimerisasi antara asam dikarboksilat dengan glikol. Polimer dilarutkan dalam monomer reaktif seperti styrene untuk menghasilkan cairan dengan viskositas rendah. Ketika mengering, monomer bereaksi dengan ikatan tak jenuh pada polimer dan berubah menjadi struktur termoset padat, Penelitian ini dilakukan untuk mengembangkan material polimer yang ramah lingkungan dan memiliki sifat mekanik dan stabilitas termal yang baik Produk polimer ini menggunakan bahan dasar poliester dengan pengisi minyak tumbuhan dari pohon jarak diperoleh dari tumbuhan jarak yang banyak tumbuh di sekitar masyarakat memberi nilai lebih karena ketersediaanya yang tak terbatas. Modifikasi poliester dan minyak tumbuhan jarak dalam penelitian ini akan dilakukan dengan cara pencampuran dan pengadukan dengan komposisi minyak tumbuhan jarak 0,2,4,6, dan 8%. Untuk katalis yang digunakan adalah Metyl Etyl Keton Peroksida (MEKPO) sebanyak 4%. Dan hasilnya akan di teliti dengan Metode Scanning electron microscope (SEM), Fourier Transform Infrared Spectroscopy (FTIR), thermogravi metric analysis (TGA), uji hardness dan uji tarik. Pengujian sifat kekerasan menunjukan penurunan nilai kekerasan hingga 11,40% dengan biopolimer poliester pengisi minyak jarak dari poliester murni yang memiliki nilai kekerasan 79,33 HD. Pengujian kekuatan tarik menunjukan peningkatan kekuatan tarik dengan variasi biopolimer poliester pengisi minyak jarak dengan kekuatan tarik sebesar 26,52 MPa. Pengujian stabilitas temperatur menunjukan penurunan stabilitas temperature T5 poliester murni hingga 31,25% dengan variasi biopolimer poliester pengisi minyak jarak yang memiliki nilai stabilitas temperatur T5 242 OC.
===========================================================================================================
Polyester is a type of thermoset polymer made from the polymerization reaction between dicarboxylic acids and glycols. The polymer is dissolved in a reactive monomer such as styrene to produce a liquid with a low viscosity. When it dries, the monomer reacts with unsaturated bonds to the polymer and turns into a solid thermoset structure. This research was conducted to develop an environmentally friendly polymeric material and has good mechanical properties and thermal stability This polymer product uses a polyester base material with a plant oil filler from a tree the distance obtained from the plants that grow a lot of distance around the community give more value because of unlimited availability. The modification of polyester and castor oil in this research will be done by mixing and stirring with the composition of vegetable oil of distance of 0.2,4,6, and 8%. For the catalyst used is Metyl Etyl Ketone Peroxide (MEKPO) as much as 4%. The results will be meticulously scanned electron microscope (SEM), Fourier Transform Infrared Spectroscopy (FTIR), thermogravi metric analysis (TGA), hardness test and tensile test. Tests of hardness properties showed a decrease in hardness value up to 11.40% with a castor oil polyester castor biopolymer of pure polyester having a hardness value of 79.33 HD. Tensile strength test showed an increase of tensile strength with variation of polyester castor oil biopolymer with tensile strength 26,52 MPa. Temperature stability testing showed a decrease in the temperature stability of T5 of pure polyester up to 31.25% with variation of polyester castor oil biopolymer having temperature stability value T5 242 OC.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | poliester, biopolimer, minyak tumbuhan, sifat mekanik, sifat termal. |
| Subjects: | Q Science Q Science > Q Science (General) |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Moch. Khabibi Al Bisthomi |
| Date Deposited: | 27 Feb 2018 04:24 |
| Last Modified: | 04 May 2020 23:33 |
| URI: | http://repository.its.ac.id/id/eprint/49408 |
Actions (login required)
 |
View Item |