Pammungkas, Fahmy (2016) Analisa Perbandingan Hasil Pengelasan Menggunakan Metode SMAW Dan Metode GMAW Terhadap Ketahanan Bending Pada Sambungan Aluminium Seri 5083. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
4311100094-Undergraduate Thesis.pdf - Published Version Download (6MB) | Preview |
Abstract
Penelitian ini bertujuan untuk menganalisa metode pengelasan mana yang lebih baik
digunakan untuk aluminium seri 5083. Pengelasan pada penelitian kali ini
menggunakan dua metode, yaitu metode pengelasan SMAW dan metode pengelasan
GMAW. Dilakukan sebuah penelitian dengan membiarkan material aluminium seri
5083 di ruangan terbuka (atmosfir) dengan melakukan pembersihan terlebih dahulu.
Pembersihan antara lain menggunakan alkohol 95%, penggerindaan, penggerindaan
dan larutan kimia NaOH 10% dengan dipanaskan sampai temperatur 720C selama 45
detik kemudian dibasuh dengan air + Nitrat Absolut 15% selama 2 menit kemudian
dicuci dengan air dingin dan air panas lalu dikeringkan. Aluminium seri 5083 H116
merupakan material paduan unsur Al (aluminium) dan unsur magnesium (Mg) yang
pembuatannya dengan cara strain hardening sehingga menciptakan material
aluminium yang anti korosi serta memiliki kekuatan yang baik. Pengelasan
aluminium memiliki permasalahan antara lain yaitu lapisan pasifnya (Al2O3) dimana
apabila senyawa ini bereaksi dengan uap air akan menjadi Hydrated alumina saat
aluminium terpapar dalam udara bebas pada waktu tertentu dan akan menimbulkan
porosity apabila dilakukan pengelasan. Dalam kasus ini, dicari metode yang tepat
supaya hasil kualitas pengelasan yang baik pada material aluminium seri 5083 H116
ini. Hasilnya dari penelitian ini adalah metode pengelasan yang paling baik untuk
menyambung material aluminium seri 5083 yaitu menggunakan metode pengelasan
GMAW dengan hasil porositas yang lebih sedikit daripada metode pengelasan
SMAW dan juga dengan menggunakan metode pengelasan GMAW lebih mudah
untuk dilakukan jika pekerjaan berada ditempat yang terjangkau oleh gas argon,
tetapi sangat susah dilakukan jika pekerjaan berada ditempat yang susah dijangkau
oleh gas argon dan terpaksa akan dilakukan pengelasan menggunakan metode
pengelasan SMAW.
======================================================================================================
This study aimed to analyze the welding method which is better used for aluminum
series 5083. Welding in the present study using two methods, namely welding
SMAW and GMAW welding method. The study conductedby letting the material
aluminium with 5083 series in the outdoor (the atmosphere) by doing the cleaning in
advance. Cleaning, among others, use alcohol 95%, grinding, grinding and chemical
solution with 10% NaOH heated to a temperature of 720C for 45 seconds and then
washed with water + Nitrate Absolut 15% for 2 minutes then washed with cold water
and hot water and then dried. Aluminum welding quality depends on the cleanliness
and dryness of the metal with a thin layer of aluminum oxide (Al2O3). The emergence
of a layer of aluminum oxide is the result of the aluminum oxide (Al) and oxygen
(O2), which is a natural protection to prevent corrosion so that the protective layer
will give you an advantage. The problem arises when the aluminum oxide has been
contaminated by moisture (H2O) because it is so hollow aluminum layer (porous) and
can absorb moisture or other hydrocarbon sources that grow thickened into Hydrated
- alumina oxide (AL2O3. H2O) has a chemical coating that causes water mixed
porosity. The result of this research is a method of welding the most good to connect
aluminum material series 5083 is using welding method GMAW with the results of
porosity less than the method of welding SMAW and also using welding GMAW is
easier to do if the work is in place that is affordable by gas argon, but it is very hard
to do if the work is in place that is difficult to reach by argon gas welding and forced
to be performed using SMAW welding methods.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSKe 671.52 Pam a |
| Uncontrolled Keywords: | Aluminium seri 5083, Al2O3, Pembersihan Aluminium seri 5083 |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials. |
| Divisions: | Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis |
| Depositing User: | Mr. Tondo Indra Nyata |
| Date Deposited: | 21 Feb 2018 07:16 |
| Last Modified: | 27 Dec 2018 04:07 |
| URI: | http://repository.its.ac.id/id/eprint/51325 |