Ardana, Dawam Putra (2018) Studi Eksperimen Metode Source Side Dan Film Side Pada Pengujian Radiografi Hasil Dari Pengelasan Metode SMAW Dengan Material SA36-15. Diploma thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2114030060_Non degree.pdf - Accepted Version Download (2MB) | Preview |
Abstract
Pada dunia pengelasan, pengujian hasil pengelasan merupakan suatu hal yang penting dengan tujuan untuk mengetahui bagaimana hasilnya, salah satu pengujian yang sering di gunakan ialah teknik radiografi (NDT).
Pada penelitian ini di lakukan pengujian Radiografi dengan perbandingan source side dan film side. Dengan menggunakan 3 (tiga) material SA36-15 dengan hasil pengelasan SMAW. Adapun material tersebut menggunakan variabel hasil pengelasan yang berbeda dari ke tiga welder. Akan tetapi pada saat pengujian radiografi digunakan standard yang sama agar dapat disimpulkan hasil dari kedua metode tersebut mana yang lebih mudah untuk diinterpretasi
Berdasarkan pengujian radiografi dapat disimpulkan bahwa Jika ingin mendapat hasil Densitas yang lebih baik sehingga film mudah untuk diinterpretasi dapat menggunakan metode source side untuk pengujian. Karena tingkat densitas yang tinggi atau lebih gelap dapat memudahkan interpretasi film untuk melihat defect. jika ingin mendapat hasil sensitivitas yang lebih baik atau dengan tingkat ketelitian yang lebih tinggi, dapat menggunakan film side sebagai metodenya. semakin kecil kawat yang terlihat maka tingkat ketelitian juga semakin bagus untuk melihat defect.
================================================================================================================== In the world of welding, testing of welding results is an important thing with the aim to know how the results. One of the most commonly used tests is the radiographic technique (NDT).
In this research is done Radiography testing with Source Side and film side comparisons, using 3(three) SA36-15 materials with SMAW welding results. The material uses different welding variables from the three welders. However at the time of radiographic testing used the same standard in order to conclude the results of both methods which are easier to interpret.
Based on radiographic testing it can be concluded that If you want to get better density results so that the film is easy to interpret can use source side method for testing. Because high or darker density levels can facilitate movie interpretation to see defects. if you want to get better sensitivity results or with a higher level of accuracy, can use film side as a method. the smaller the wire is visible then the level of accuracy is also better to see the defect.
| Item Type: | Thesis (Diploma) |
|---|---|
| Additional Information: | RSMI 671.52 Ard s |
| Uncontrolled Keywords: | NDT Testing; SMAW welding; Radiography testing; Source side; Film side |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA492.W4 Welded joints T Technology > TJ Mechanical engineering and machinery |
| Divisions: | Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3 |
| Depositing User: | Dawam Putra Ardana |
| Date Deposited: | 03 May 2018 03:04 |
| Last Modified: | 22 Jun 2020 07:54 |
| URI: | http://repository.its.ac.id/id/eprint/51344 |
Actions (login required)
 |
View Item |