Amhudo, Rasyiid Lathiif (2018) Perilaku Mekanik Beton Cetak Kering Dengan Semen OPC Dan PPC. Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 03111550020013-Master Thesis.pdf]
Preview
Text
03111550020013-Master Thesis.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Beton adalah material konstruksi yang paling banyak digunakan di dunia, seiring juga seiring dengan meningkatnya kebutuhan ekonomi dibidang pembangunan maka kemudian dikembangkan teknologi pracetak yang mengarah pada industrialisasi Beton bertulang pracetak pertamakali digunakan di Amerika Utara pada penggunaan sebagai pipa pembuangan limbah dan air hujan pada beberapa dekade yang lalu. Salah satu material penyusun yang sering digunakan dalam teknologi pracetak adalah beton normal. Penggunaan sistem beton pracetak menawarkan beberapa keunggulan seperti ereksi cepat, kualitas yang lebih tinggi, biaya proyek yang lebih rendah, keberlanjutan yang lebih baik, dan meningkatkan kesehatan dan keselamatan kerja. Pada umumnya praktek dilapangan para praktisi beranggapan perilaku yang ada pada beton normal dengan sistim cetak basah (wet cast) mendekati kesamaan dengan sistim cetak kering (dry cast). Pada kedua jenis sistim cetak beton tersebut memiliki perilaku yang dipengaruhi oleh banyak faktor, meliputi adalah kuat tekan beton, umur pembebanan beton, tipe kondisi perawatan dari beton, tipe dan jenis semen, tipe dari agregat, rasio air dan semen (water-cement ratio), campuran adukan beton, ukuran dan bentuk dari meterial, tipe dan durasi dari pembebanan. Peraturan dan standar yang ada banyak didapat berdasarkan penelitian dan pengujian beton cetak basah, adakah pengeruh yang timbul akibat berbedanya sisim cetak yang diterapkan pada semen OPC dan PPC, oleh karena itu dalam penelitian ini diteliti mengenai beton sistim cetak kering dengan berbagai pengujian, meliputi uji kuat tekan beton silinder Diameter 4 x 8 inch cm pada perkembangan umur 1,7,14,21,28,56 hari, kuat belah beton dengan diameter silinder yang sama, kuat lentur balok 15 x 15 x 60 cm, serta pengamatan bentuk perilaku retak dan kegagalan pada sampel beton cetak kering, semua sampel dibuat dengan dua tipe semen, yaitu OPC dan PPC. Hasil penelitian ini diharapkan dapat mengetahui perkembangan dan perbedaan kinerja dan perilaku sistim cetak pada beton terhadap kedua tipe semen tersebut dalam penggunaanya dilapangan.
==================================================================================================
Concrete is the most widely used construction material in the world, along with the increasing economic needs in the field of development then developed precast technology that leads to industrialization Pre-casted reinforced concrete was first used in North America on use as a waste and rainwater disposal pipe several decades ago. One of the constituent materials often used in precast technology is normal concrete. The use of precast concrete systems offers several advantages such as rapid erection, higher quality, lower project costs, better sustainability, and improved occupational health and safety. In general practitioners practice the behavior of existing concrete in normal concrete with a wet cast system close to the similarity with the dry cast system. In both types of concrete molding systems have behavior influenced by many factors, including concrete compressive strength, concrete loading time, type of treatment conditions of concrete, type and type of cement, type of aggregate, water-cement ratio, mixed mixture of concrete, size and shape of the meterial, type and duration of loading. Rules and standards are widely available on the basis of research and testing of wet concrete, is there any applicator arising from the different producted sides applied to OPC and PPC cement, therefore in this study examined the concrete dry printing system with various tests, including strong test press cylinder concrete Diameter 4 x 8 inch cm at development of age 1,7,14,21,28,56 day, concrete strength with same cylinder diameter, bending strength of beam 15 x 15 x 60 cm, and observation of behavior form of crack and failure on dry concrete sample samples, all samples were made with two types of cement, ie OPC and PPC. The result of this research is expected to know the development and difference of performance and behavior of production system on concrete to both types of cement in its use in field.

Item Type: Thesis (Masters)
Additional Information: RTS 620.136 Amh p-1 3100018074414
Uncontrolled Keywords: drycast; kuat tekan; kuat belah; kuat lentur; OPC; PPC; compressive strength; split tensile strength; flexural strength
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TA Engineering (General). Civil engineering (General) > TA440 Concrete--Cracking.
Divisions: Faculty of Civil, Planning, and Geo Engineering (CIVPLAN) > Civil Engineering > 22101-(S2) Master Thesis
Depositing User: Amhudo Rasyiid Lathiif
Date Deposited: 03 Jul 2018 04:17
Last Modified: 29 Sep 2020 03:15
URI: http://repository.its.ac.id/id/eprint/51594

Actions (login required)

View Item View Item