Afnani, Fawait (2015) Sintesis Senyawa Kompleks Polimer {[Ni(NCS)2(2,4,5-Trifenil-1H-Imidazol)2(H2O)2]·DMF}n sebagai Material Penyimpan Hidrogen. Masters thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
1412201019-Master_Thesis.pdf - Published Version Download (1MB) | Preview |
Abstract
Senyawa kompleks polimer {[Ni(NCS)2 (2,4,5-trifenil-1H- imidazol)2 (H2 O)2 ]•DMF}n menunjukkan bahwa kompleks polimer tersebut mempunyai pori dan luas permukaan yang kecil. Kompleks polimer ini digunakan sebagai material untuk menyimpan hidrogen. Pada penelitian ini telah dilakukan sintesis {[Ni(NCS)2 (2,4,5-trifenil-1H-imidazol)2 (H2 O)2 ]•DMF}n menggunakan metode solvotermal. Prekursor yang digunakan adalah NiCl2 .6H2 O dan NH4 SCN serta 2,4,5-Trifenil-1H-Imidazol dalam pelarut DMF dengan rasio molar = 1 : 4 : 2. Larutan tersebut di refluks pada suhu 70°C selama 3 jam, kemudian dipanaskan pada suhu 120 °C di dalam autoclave selama 2 hari. Larutan hasil pemanasan tersebut selanjutnya diuapkan pada suhu 100 °C selama 3 jam dalam kondisi vakum. Hasil yang diperoleh merupakan padatan berwarna hijau kekuningan. Hasil analisis spektroskopi UV-Vis kompleks polimer menunjukkan nilai λmaks 431 nm. Pada spektrum FT-IR menunjukkan adanya vibrasi Ni-
N(imidazol) yang muncul pada 378 cm-1. Berdasarkan pada analisis kandungan unsur untuk C49 H43 NiN7 O3 S2 dengan massa molekul relatif (805,85 g/mol) mempunyai kadar Ni (7,28%); C (72,23 %); H (5,87 %); N (11,97 %); S (8,03 %). Stabilitas suhu kompleks polimer ini dapat dicapai hingga 300 °C . Foto hasil SEM menunjukkan kompleks polimer ini cukup homogen dengan ukuran partikel 7-12µm. Pada hasil adsorpsi terhadap hidrogen kapasitas yang diperoleh 2,048% berat.
=============================================================================================
Polymer complex of {[Ni(NCS)2 (2,4,5-trifenil-1H- imidazol)2 (H2 O)2 ]•DMF}n showed that the complex polymer has small pore and small surface area. This polymer complex is used as material for hydrogen storage. This research was synthesized {[Ni(NCS)2 (2,4,5-trifenil-1H- imidazol)2 (H2 O)2 ]•DMF}n using solvothermal method by ratio molar = 1 : 4 : 2 mixing of NiCl2 .6H2 O and NH4 SCN with 2,4,5-Triphenyl-1H-Imidazole as precursors in DMF. The solution is refluxed at at 70 oC for 3 h, and then heated at 120 °C using autoclave for 2 days. Subsequently, the solution is evaporated at 100 °C for 3 h in vacuum condition. The synthesis result obtained solid green-yellow powder. The result of UV-Vis spectroscopy analysis of this sample shows 431 nm of λmax . FT-IR spectrum analysis showed vibration of Ni-N(imidazole) appears at 378 cm-1. Elemental analysis of C49 H43 NiN7 O3 S2 (Mr = 805.85 g/mol) has percentage of Ni (7.28%); C (72.23%); H (5.87%); N (11.97%) and S (8.03%). Thermal stability of the polymer complex can be achieved up 300 oC. SEM photo showed reasonably homogeneous which has 7-12 μm of particle size. The hydrogen storage capacities of up t o 2.048 wt.% by kompleks polimer {[Ni(NCS)2 (2,4,5- trifenil-1H-imidazol)2 (H2 O)2 ]•DMF}n.
| Item Type: | Thesis (Masters) |
|---|---|
| Additional Information: | RTKi 547.7 Afn s |
| Uncontrolled Keywords: | 2,4,5-trifenil-1H-imidazol, adsorpsi hidrogen, kompleks polimer, kompleks nikel(II) isotiosianat, 2,4,5-Triphenyl-1H-Imidazole, complex polymers, complex of Ni(II), hydrogen adsorption, nickel(II) isothiocyanato complexes |
| Subjects: | Q Science > QD Chemistry Q Science > QD Chemistry > Polymerization Q Science > QD Chemistry > QD547 Flocculation, precipitation, adsorption, etc. T Technology > TP Chemical technology > TP1140 Polymers |
| Divisions: | Faculty of Mathematics and Science > Chemistry > 47101-(S2) Master Thesis |
| Depositing User: | Eny Widiastuti - |
| Date Deposited: | 21 May 2018 08:01 |
| Last Modified: | 24 Aug 2018 01:50 |
| URI: | http://repository.its.ac.id/id/eprint/51921 |
Actions (login required)
 |
View Item |