Rahmawati, Hani (2015) Perbandingan Template Organik TPABr Dan TPAOH Pada Sintesis ZSM-5 Dari Kaolin Bangka. Undergraduate thesis, Institut Technology Sepuluh Nopember.
Preview |
Text
1411100077-Undergraduate Thesis.pdf - Published Version Download (1MB) | Preview |
Abstract
Sintesis ZSM-5 dari kaolin Bangka dan abu sekam padi sebagai sumber silika dan alumina telah dipelajari. ZSM-5 disintesis untuk membandingkan template organik TPABr dan TPAOH menggunakan metode hidrotermal dengan variasi waktu kristalisasi 3, 6, 9, 12, 24, dan 48 jam. Pada penelitian ini ZSM-5 disintesis dengan komposisi molar 10Na2O : 100SiO2 : 2Al2O3 : 2000H2O : 20TPA menggunakan metode hidrotermal pada suhu 175 °C. Hasil padatan dikarakterisasi menggunakan teknik difraksi sinar-X (XRD) dan spektroskopi inframerah (FTIR) yang menunjukkan bahwa ZSM-5 mulai terbentuk pada sampel dengan waktu kristalisasi 24 dan 48 jam menggunakan template organik TPABr dan TPAOH. Berdasarkan intensitas yang diperoleh, sampel dengan template organik TPABr menghasilkan kristalinitas ZSM-5 yang lebih tinggi dan intensitas fasa analsim yang rendah. Pembentukan kristal ZSM-5 lebih cepat pada sampel yang menggunakan template organik TPABr dibandingkan template organik TPAOH dengan lama waktu kristalisasi 24 jam.
==================================================================================================
Synthesis of ZSM-5 from kaolin Bangka and rice husk ash as a source of silica and alumina has been studied. ZSM-5 was synthesized to compare the organic templates TPABr and TPAOH using hydrothermal method with variation of crystallization time 3, 6, 9, 12, 24, and 48 hours. In this research ZSM-5 synthesized with molar composition 10Na2O : 100SiO2 : 2Al2O3 : 2000H2O : 20TPA using hydrothermal method in 175 °C temperature. The solid results were analyzed using X-ray diffraction (XRD) and infrared spectroscopy (FTIR) showed that ZSM-5 began to form on the sample at the time 24 and 48 hours of crystallization using both organic templates TPABr and TPAOH. Based on the intensity obtained, the sample with an organic template TPABr produced a higher ZSM-5 crystallinity and low intensity of analcime phase. The formation of ZSM-5 crystalline was faster in the sample using organic templates TPABr compared to organic templates TPAOH at 24 hours of crystallization time.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSKi 549.68 Rah p |
| Uncontrolled Keywords: | Kaolin Bangka, abu sekam padi, sintesis ZSM-5, TPABr, TPAOH. |
| Subjects: | Q Science > QD Chemistry |
| Divisions: | Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis |
| Depositing User: | Mr. Tondo Indra Nyata |
| Date Deposited: | 04 Jun 2018 05:58 |
| Last Modified: | 04 Jun 2018 05:58 |
| URI: | http://repository.its.ac.id/id/eprint/51981 |
Actions (login required)
 |
View Item |