Azhar, Zulfikar Rizky (2018) Analisis Pengaruh Variasi Temperatur Fluida Dalam Dan Variasi Jenis Coating Terhadap Karakteristik Korosi Di Bawah Insulasi Pada Pipa Baja ASTM A53 Grade B. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511440000119-Thesis_undergraduate.pdf - Accepted Version Download (8MB) | Preview |
Abstract
CUI adalah suatu bentuk korosi yang disebabkan oleh
adanya uap air dalam bahan insulasi pipa. Korosi dibawah insulasi
(CUI) sulit diamati keberadaannya, karena terjadinya korosi
tersebut berada diantara permukaan pipa dan bahan insulasi yang
di pasang pada permukaan luar pipa. Penelitian ini memiliki tujuan
untuk mengetahui pengaruh variasi temperatur fluida dalam dan
variasi jenis coating terhadap karakteristik korosi bagian luar pipa
baja ASTM A53 Grade B dengan material insulasi silica aerogel
dan alumunium foil. Pipa yang akan diuji pada temperatur fluida
bagian dalam sebesar 50oC, 60oC dan 70oC dengan variasi jenis
coating epoxy, alkyd, PTFE dan polyurethane. Dengan kondisi
lingkungan luar menggunakan kandungan 150ppm NaCl.
Rangkaian tersebut diuji selama 14 hari dengan metode immerse.
Untuk menganalisa karakteristik korosi yang terjadi dilakukan
pengujian OM,SEM, XRD, dan uji Weight Loss. Hasil pengujian
OM menunjukkan bahwa seiring kenaikan temperatur lapisan
coating akan rusak. Sedangkan hasil SEM menunjukan bahwa jenis
korosi yang timbul ialah uniform corrosion. Untuk uji weight loss
menunjukkan bahwa dengan kenaikan temperatur maka laju korosi
semakin meningkat dengan dengan efisiensi lapisan coating yang
paling tinggi ke rendah ialah coating epoxy, PTFE, PU dan alkyd.
Sementara hasil pengujian XRD menunjukan produk korosi yang
terbentuk adalah FeS , FeCl2 dan Fe2O3. =============== CUI is a form of corrosion caused by the presence of water vapor
in pipeline insulation materials. Corrosion under insulation (CUI)
is difficult to observe, since the corrosion occurs between the
surface of the pipe and the insulating material placed on the outer
surface of the pipe. This research has purpose to know the influence
of variation of fluid temperature in and variation of coating type to
corrosion characteristics of outer part of steel pipe ASTM A53
Grade B with insulation material of silica aerogel and alumunium
foil. Pipes to be tested at internal fluid temperature of 50oC, 60oC
and 70oC with variations of epoxy, alkyd, PTFE and polyurethane
coatings. With outside environmental conditions using 150ppm
NaCl content. The circuit will be tested for 14 days with the
immerse method. To analyze the corrosion characteristics that
occur are used OM, SEM, XRD, and Weight Loss test. OM test
results show that as the coating temperature rise will be damaged.
While the SEM results showed that the type of corrosion that arises
is uniform corrosion. For weight loss test showed that with
increasing temperature the corrosion rate is increasing with coating
efficiency of highest to low coating is epoxy, PTFE, PU and alkyd..
While XRD test results show that corrosion product is FeS , FeCl2
dan Fe2O3.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Corrosion under insulation (CUI) , Silica Aerogel, Coating, Temperatur, corrosion |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives T Technology > TA Engineering (General). Civil engineering (General) > TA491 Metal coating. |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Azhar Zulfikar Rizky |
| Date Deposited: | 09 Oct 2018 07:32 |
| Last Modified: | 12 Mar 2021 04:52 |
| URI: | http://repository.its.ac.id/id/eprint/52686 |
Actions (login required)
 |
View Item |