Prasetyo, Mirza Farhan (2018) Pengaruh Polutan Fly Ash Paiton Terhadap Isolator Keramik yang Dilapisi Senyawa Silikon. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
07111440000074-Undergraduate_Theses.pdf - Accepted Version Download (4MB) | Preview |
Abstract
Limbah dari pembakaran batubara di PLTU Paiton menghasilkan abu terbang (fly ash) yang dapat mengotori peralatan tegangan tinggi disekitar PLTU Paiton. Oleh sebab itu dilakukan penelitian untuk mengetahui pengaruh polutan fly ash Paiton terhadap isolator keramik yang dilapisi senyawa silikon. Pengujian dilakukan didalam sebuah lemari uji dengan mengatur kelembaban udara didalamnya. Sebelum dilakukan pengujian, terlebih dahulu isolator divariasikan menjadi isolator yang dilapisi silikon dengan yang tidak dilapisi silikon. Kemudian keduanya diberikan polutan fly ash Paiton dengan bobot 50 gram dan 150 gram. Pengujian yang dilakukan adalah pengujian arus bocor isolator dan pengujian tegangan flashover isolator. Pengujian arus bocor menggunakan metode step voltage dan pengujian flashover menggunakan metode short time test. Hasil pengujian arus bocor adalah polutan dengan bobot polutan paling besar yang menempel pada permukaan isolator akan membuat arus bocor isolator lebih besar dibandingkan dengan arus bocor pada isolator dengan bobot polutan yang lebih sedikit. Pelapisan silikon pada isolator membuat nilai arus bocor isolator akan lebih kecil dibandingkan dengan isolator tanpa pelapisan silikon pada tingkat bobot polutan yang sama. Pada pengujian flashover, isolator dengan silikon maupun isolator tanpa silikon belum menunjukkan adanya fenomena flashover pada tegangan >80 kV. Namun pada tegangan 40 kV hingga 80 kV terlihat kenaikan arus bocor akibat pengaruh kenaikan tegangan dan juga pada pengujian dengan kelembaban 80% menghasilkan arus bocor yang lebih besar dibandingkan pengujian dengan kelembaban 50%.============= The waste generated by coal combustion in the Paiton Power Plant produces fly ash which can contaminate high voltage equipment around the Paiton power plant. Therefore, a research was conducted to determine the effect of Paiton fly ash pollutants on ceramic insulators coated with silicon compounds. The test is done inside a test chamber by adjusting the humidity inside. Prior to testing, firstly insulators varies into silicon-coated insulator and non silicone-coated insulator. Then, both are given Paiton fly ash pollutants with a weight of 50 grams and 150 grams. The research is the testing of leakage current of insulator and flashover voltage of insulator test. Leakage current test using step voltage method and flashover test using short time test method. Leakage current test results are the pollutants with the largest pollutant weight attached to the insulator surface will make the leakage current of the insulator is greater than the leakage current on the insulator with less pollutant weight. The silicon coating on the insulator makes the insulator leakage current value smaller than the insulator without silicone coating at the same level of pollutant weight. In flashover testing, silicone insulator and isolator without silicon have not shown flashover phenomenon at> 80 kV. However, at a voltage of 40 kV to 80 kV, a rise in the leakage current due to the effect of the voltage rise and also on the test with 80% humidity produces a larger leakage current than the 50% humidity test.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Arus Bocor; Fly Ash; Isolator Keramik; NSDD; Senyawa Silikon; dan Tegangan Flashover; Ceramic Insulators; Flashover Voltage; Fly ash; Leakage Current; NSDD; and Silicon Grease |
| Subjects: | T Technology > TK Electrical engineering. Electronics Nuclear engineering T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK3401 Insulation and insulating materials |
| Divisions: | Faculty of Electrical Technology > Electrical Engineering > 20201-(S1) Undergraduate Thesis |
| Depositing User: | Prasetyo Mirza Farhan |
| Date Deposited: | 20 Jul 2018 08:56 |
| Last Modified: | 16 Apr 2021 04:38 |
| URI: | http://repository.its.ac.id/id/eprint/52882 |
Actions (login required)
 |
View Item |