Analisis Pengaruh Variasi Larutan Asam (HNO3, H2SO4, HCl) Terhadap Proses Ekstraksi Lithium Pada Lumpur Sidoarjo Menggunakan Metode Hidrometalurgi.

Muharrom, Muhammad Iqbal (2018) Analisis Pengaruh Variasi Larutan Asam (HNO3, H2SO4, HCl) Terhadap Proses Ekstraksi Lithium Pada Lumpur Sidoarjo Menggunakan Metode Hidrometalurgi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02511440000078-Undergraduate_Theses.pdf]
Preview
Text
02511440000078-Undergraduate_Theses.pdf - Accepted Version

Download (5MB) | Preview

Abstract

Lithium merupakan suatu mineral yang banyak digunakan pada pembuatan baterai yang dapat di isi ulang (rechargeable). Salah satu sumber lithium adalah berasal dari geothermal atau fluida yang keluar dari dalam bumi, di Indonesia terdapat sumber lithium geothermal yaitu lumpur lapindo Sidoarjo. Pada penelitian ini dilakukan proses ekstraksi lithium melalui metode hidrometalurgi dengan variasi larutan asam (HNO3, H2SO4, HCl) untuk mengetahui pengaruhnya terhadap morfologi padatan yang terbentuk dan efisiensi pada proses ekstraksi. Proses ekstraksi ini dilakukan dengan proses milling dengan ball mill selama 3 jam kemudian dikalsinasi dengan furnace pada temperatur 700ºC selama satu jam, kemudian melakukan penambahan NaOH sebanyak 200ml pada lumpur kering sidoarjo. Setelah proses pencampuran hingga menjadi slurry, dilakukan leaching dengan variasi asam (HNO3, H2SO4, HCl), penambahan Ca(OH)2, dan Na2CO3. Dari pengujian XRD menunjukkan terbentuknya Li2CO3 dengan intensitas tertinggi yaitu pada peak posisi 2θ 29,47o intensitasnya 1000 pada variabel lautan asam HNO3. Pada saat setelah ekstraksi didapatkan morfologi kristal yang berbeda dengan senyawa lithium yang berbeda juga hal ini dikarenakan pada kadar penambahan reaktan Na2CO3. Nilai efektifitas reaksi tertinggi pada variabel HCl yaitu 0,093 ppm, kedua HNO3 0,022 ppm dan ketiga H2SO4 0,013 ppm, sedangkan nilai effisiensi ekstraksi tertinggi terdapat pada variabel H2SO4 yaitu 69%, kedua HNO3 yaitu 64% dan ketiga HCl yaitu 54%. Hal ini dikarenakan nilai keasaman larutan, potensial reduksi dan energi bebas gibs senyawa lithium yang terbentuk pada tiap variabel.
Kata kunci: Hidrometalurgi, Lithium, Lumpur Sidoarjo, Asam
=============== Lithium is a mineral that used widely in rechargeable batteries. One source of lithium is derived from geothermal or fluid out of the earth, in Indonesia there is a source of lithium geothermal Sidoarjo’s Dry Mud. In this research, Lithium extraction process is done through Hydrometallurgy method with acid solution variation to know its effect on morphology and efficiency in extraction process. Acid solution is done with variations of HNO3, H2SO4, HCl. This extraction process is carried out by milling with ball mill for 3 hours and roasting 700ºC for 1 hours, next mixing 200m NaOH and Sidoarjo’s Dry Mud. After mixing the slurry, leaching with acid variation HNO3, H2SO4, HCl ,then Ca(OH)2, and Na2CO3 are added. From the XRD results, the formation of Li2CO3 with the highest intensity that is at peak position 2θ 29,47o with intensity of 1000 at variabel HNO3 acid solution. At the time after extraction, morphology obtain the different crystals with different lithium compounds was also due to the addition of Na2CO3 reactants. The highest value of reaction effectivity on HCl variable is 0.093 ppm, both HNO3 0.022 ppm and third H2SO4 0.013 ppm, while the highest extraction efficiency value is in H2SO4 variable is 69%, both HNO3 is 64% and third HCl is 54%. This is due to the acidity value of the solution, the reduction potential and the libium-free gibs free energy formed on each variable.
Keywords: Hydrometallurgy, Lithium, Acid, Sidoarjo’s Mud

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 669.028 3 Muh a-1
Uncontrolled Keywords: Hydrometallurgy, Lithium, Acid, Sidoarjo’s Mud, Hidrometalurgi, Lithium, Lumpur Sidoarjo, Asam
Subjects: Q Science > QD Chemistry > QD63 Extraction
T Technology > TN Mining engineering. Metallurgy > TN688 Hydrometallurgy
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Muharrom Muhammad Iqbal
Date Deposited: 29 Nov 2018 03:58
Last Modified: 23 Apr 2021 04:48
URI: http://repository.its.ac.id/id/eprint/53170