Analisa Pengaruh Konsentrasi Cetyltrimethyl Ammonium Bromide Sebagai Template Terhadap Pembentukan Silika Mesopori MCM-41 Dari Sekam Padi

Ervianto, Yohan (2018) Analisa Pengaruh Konsentrasi Cetyltrimethyl Ammonium Bromide Sebagai Template Terhadap Pembentukan Silika Mesopori MCM-41 Dari Sekam Padi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Preview	Text 02511440000081_Laporan Tugas Akhir.pdf - Accepted Version Download (2MB) | Preview
	Text 02511440000081-Undergraduate_Theses.pdf - Published Version Restricted to Repository staff only Download (2MB)

Abstract

Sekam padi adalah limbah pertanian. Silika merupakan komponen inorganik dari sekam padi, dimana dengan melakukan proses ekstraksi dapat dihasilkan silika dengan kemurnian yang tinggi. Silika hasil ekstraksi bisa digunakan sebagai prekursor untuk sintesis mesoporous silika sebagai pengganti TEOS. Tujuan dari penelitian ini yaitu mensintesis mesopori silika menggunakan metode sol-gel dengan Variabel konsentrasi CTAB. kemudian dititrasi dengan asam asetat dan selanjutnya dilakukan proses hidrotermal. Berdasarkan penelitian yang telah dilakukan, terbentuk material silika dengan struktur kristal amorf. Ukuran partikelnya 243 nm dengan bentuk seperti terumbu karang. Poriporinya membentuk strukur heksagonal yang merupakan struktur dari MCM-41. Dari pengujian adsorption-desorption isotherms untuk sampel penambahan 2% CTAB luas permukaannya adalah 1291.436 m2/g, volume total porinya adalah 1.601 cc/g, dan ukuran diameter porinya adalah 4.95764 nm.
=============================================================================================================
Rice husk is an agricultural waste that can be used to produce high-purity amorphous silica. To obtain pure silica, first, use acid leching treatment to the rice husk, followed by heat treatment at 600oC and then by sol-gel method to produce amorphous silica. In this research synthesis of mesoporous silica MCM-41 using sol-gel method with the assisted of Cetyl Trimethyl Ammonium BromideCTAB as template. Sol gel method include acetic acid titration and hydrothermal process in the teflon line-autoclave. X-ray diffraction-XRD showed that mesoporous silica has amorphous liked-crystal structure, hence scanning electron microscope-SEM shown microstructure such as coral reefs and have particle sizes 243 nm. Fourier Transformed Infrared-FTIR explained that Si-O-Si bond groups identified in the sample. Transmission electron microscope-TEM image have proved the porous structure on the silica surface. Pores formed a hexagonal structure which is a typical structure of MCM-41. From the adsorption-desorption isotherms test a sample 2% CTAB show the surface area is 1291,436 m2 / g, total volume of the pellet is 1,601 cc / g, and pore diameter is 4.95764 nm.

Item Type:	Thesis (Undergraduate)
Additional Information:	RSMt 620.5 Erv a-1 3100018075882
Uncontrolled Keywords:	silika mesopori, sekam padi, sol-gel, konsentrasi, CTAB
Subjects:	T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	ervianto yohan
Date Deposited:	05 Dec 2018 17:12
Last Modified:	02 Oct 2020 04:50
URI:	http://repository.its.ac.id/id/eprint/53207

Actions (login required)

View Item