Himawan, Arif fajar (2018) Analisa Pengaruh pH, Kecepatan Putar, dan Perbandingan Volume Inhibitor berbasis Parasetamol dan Imidazoline Terhadap Laju Korosi Baja st41 Di Lingkungan Co2 Menggunakan Metode Rotating Disk Elektrode. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511340000135-undergraduate_thesis.pdf - Accepted Version Download (5MB) | Preview |
Abstract
Percobaan korosi CO2 telah dilakukan menggunakan metode Rotating disc electrode. Fenomena korosi yang sering terjadi pada pipa baja karbon yang digunakan dalam induatri pertambangan minyak di sebabkan oleh gas CO2 dan asam - asam organic yang terlarut dalam air. Untuk menghindari atau memperkecil kerugian yang disebabkan oleh korosi diperlukan adanya suatu pencegahan atau pengendalian korosi, salah satunya dengan penambahan inhibitor. Penelitian ini bertujuan untuk mengetahui pengaruh fraksi volume inhibitor parasetamol : imidazoline dan kecepatan putar terhadap laju korosi dengan pengaruh pH 4 dan pH 6 pada baja St41 di lingkungan yang mengandung gas CO2. Pada penelitian ini digunakan media elektrolit NaCl 3,5% dengan variasi kecepatan putaran yaitu 100 rpm dan 200 rpm pada pH 4 dan 6 dengan perbandingan volume inhibitor paracetamol : Imidazoline sebesar 20:80, 30:70, 50:50, 70:30, 80:20 dalam satuan persen pada specimen baja St41 dengan diameter 2 cm dan tebal 0,5 cm. Untuk mengetahui laju korosi yang terjadi menggunakan metode weight loss dengan alat Rotating Disc Electrode (RDE) selama 10 hari. Kemudian digunakan pengujian XRD untuk menganalisa senyawa dari korosi tersebut. Dan pengujian FTIR untuk mengetahui gugus fungsi dari inhibitor dan sampel tersebut. Hasil dari penelitian ini didapatkan bahwa berdasarkan uji weight loss telah didapatkan nilai effisiensi tertinggi yaitu pada fraksi 50%:50% pH 4 dan kecepatan putar 100 RPM dengan nilai efisiensi 71%. Sedangkan pada sampel pH 6 efisiensi tertinggi ada pada fraksi 50% : 50% dengan kecepatan putar 100 RPM dengan nilai efisiensi 66%. Pada pengujian FTIR specimen dengan fraksi 50% : 50% pH 4 100 RPM terdapat gugus fungsi dari kedua inhibitor tersebut yaitu N-H, C-H, dan C=O. Pengujian XRD menunjukkan adanya senyawa iron nitride yang terbentuk karena reaksi yang terjadi antara Fe dan atom nitrogen pada pyridine.
===========================================================
CO2 corrosion experiments have been performed using Rotating disc electrode method. The frequent corrosion phenomenon in carbon steel pipes used in the oil mining industry is caused by CO2 gas and organic acids dissolved in water. To avoid or minimize the loss caused by corrosion is required a prevention or control of corrosion, one of them with the addition of inhibitor. The present study used the fraction of the volume of paracetamol inhibitors: imidazoline and rotational velocity against the corrosion rate with the effect of pH 4 and pH 6 on St41 steels in an environment containing CO2 gas. In this research used 3.5% NaCl electrolyte media with variation of rotation speed that is 100 rpm and 200 rpm at pH 4 and 6 with ratio of volume of paracetamol inhibitor: Imidazoline 20:80, 30:70, 50:50, 70:30, 80:20 in units per cent on St41 steel specimens with a diameter of 2 cm and 0.5 cm thick. To know the corrosion rate that happened using weight loss method with Rotating Disc Electrode (RDE) for 10 days. In addition, XRD testing is used to analyze the compounds of the corrosion. And FTIR testing to determine the functional groups of the inhibitor and the sample. The result of this research shows that based on the weight loss test, the highest efficiency is 50%: 50% pH 4 and 100 RPM rotation efficiency with 71% efficiency. While on the sample pH 6 dental efficiency adapa at fraction 50%: 50% with rotation speed 100 RPM with efficiency value 66%. In the FTIR test in the specimen with a 50%: 50% pH 4 100 RPM fraction there was a functional group of both inhibitors the result is N-H, C-H, dan C=O. XRD testing shows the presence of iron nitride compounds that are formed due to reactions that occur between Fe and nitrogen atoms in pyridine.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | gas CO2, imidazoline, kecepatan putar ,korosi, paracetamol, pH |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives |
| Depositing User: | arif fajar himawan |
| Date Deposited: | 21 Jun 2021 02:23 |
| Last Modified: | 21 Jun 2021 02:23 |
| URI: | http://repository.its.ac.id/id/eprint/54394 |
Actions (login required)
 |
View Item |