Furqana, Fawaida (2018) Tegangan Maksimum (V maks) Elektroda pada Air Laut Untuk Energi Terbarukan Melalui Eksperimen Air Garam. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
01111440000018-Undergraduate_Theses.pdf - Accepted Version Download (716kB) | Preview |
Abstract
Penelitian yang dilakukan pada tugas akhir ini menggunakan metode sel elektrokimia. Dalam sel elektrokimia terdapat dua penampang elektroda yaitu katoda dan anoda. Pada proses pengujian, katoda yang digunakan yaitu tembaga dan anoda yang digunakan adalah seng. Penelitian ini bertujuan untuk mengetahui pengaruh molaritas garam terhadap nilai tegangan dan arus, mengetahui pengaruh luas penampang elektroda terhadap hasil tegangan dan arus, perbedaan nilai arus dan tegangan jika diberikan hambatan maupun tidak, dan mengetahui nilai daya maksimum dari hasil tegangan dan arus tersebut. Pada penelitian ini elektroda disusun secara seri sebanyak 14 sel, dengan variasi massa garam yaitu 5,7,8,9,10,11,12,13,15,dan 20 gr. Variasi garam tersebut diberikan sesuai dengan kadar garam di air laut, air atau pelarut yang digunakan sebanyak 100 ml. Hasil yang diperoleh adalah nilai tegangan, arus, serta daya dimana hasil arus maksimum yang dihasilkan yaitu ada pada massa garam 9 gr, dengan daya maksimum yang diperoleh juga ada pada massa garam 9 gr. Nilai tersebut berada dibagian titik puncak pada massa garam 9 gr, setelah penambahan garam berikutnya hasil arus semakin turun terus menerus seiring penambahan garam. Hal ini terjadi karena air tidak mampu untuk mengurai NaCl menjadi Na+ dan Cl-. ======================================================================Research done on this final project using electrochemical cell method. In the electrochemical cell there are two electrode sections of cathode and anode. In the test the cathode used is the copper and the the anode used is the xinc. This study aims to determine the effect of salt molarity on the value of voltage and current, to know the effect of electrode cross-sectional area to the result of voltage and current, the difference of current and voltage values if given resistance or not and, knowing the maximum power value of the voltage and current results. In this study electrode arranged in series as much 14 cell with variations of salt mass that is 5,7,8,9,10,11,12,13,15, and 20 gr. The salt variation is given according to the salt content in seawater, water or solvent used as much as 100 ml. The result is the value of voltage, current, and power where the resulting maximum current yields are present at a slat massof 9 grams, with the maximum power being obtained is also present at a salt mass 9 grams. The value is located at the peak point on a salt mass of 9 grams, after the addition of the next salt the current results more continuously as the addition of salt. This occurs because water is unable to break down NaCl into Na+ and Cl-.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Arus, Daya, Molaritas Garam, Sel Elektrokimia, Tegangan |
| Subjects: | Q Science > QD Chemistry > QD553 Electrochemistry. Electrolysis |
| Divisions: | Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis |
| Depositing User: | Fawaida Furqana |
| Date Deposited: | 28 Jun 2021 07:16 |
| Last Modified: | 28 Jun 2021 07:16 |
| URI: | http://repository.its.ac.id/id/eprint/56557 |
Actions (login required)
 |
View Item |