Aliviyan, Moch. Farobi (2018) Pengaruh Bevel Groove dan V Groove pada Low Carbon Steel SA36 Menggunakan Las SMAW dengan Elektroda E7016 Terhadap Kekuatan Tarik, Makro Etsa, dan Kekerasan - The Effect Bevel Groove And V Groove At Low Carbon Steel SA 36 Using Welding Of SMAW With Electrode E7016 Toward Tensil Strength, Hardness, And Macro Etching. Diploma thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
10211500000033-Non_Degree.pdf - Accepted Version Download (2MB) | Preview |
Abstract
Perkembangan ilmu pengetahuan dan teknologi (IPTEK) tepatnya pada teknologi pengelasan dewasa ini telah banyak dipergunakan secara luas pada penyambungan batang-batang pada konstruksi bangunan baja dan konstruksi mesin. Sehingga pengetahuan mengenai teknologi pengelasan sangat diperlukan untuk mencapai kesesuaian antara hasil yang diinginkan dengan proses pengelasan yang mungkin dilakukan agar diperoleh hasil yang optimal.
Dalam tugas akhir ini pengelasan yang digunakan las SMAW. Salah atu jenis sambungan las yang perlu dikaji lebih lanjut adalah sambungan las dengan groove v dan bevel. Pemilihan jenis groove tersebut didasarkan pada adanya kecenderungan pemakaiannya yang lebih umum. Selanjutnya untuk mengetahui kekuatan sambungan dari kedua bentuk groove dengan mengamati sifat mekanik dan struktur makro.
Dari hasil pengujian yang telah dilakukan pengelasan SMAW pada baja SA 36 dengan bentuk bevel groove lebih kuat dibandingkan v groove dikarenakan nilai kekuatan tarik yang diperoleh pada bentuk bevel groove lebih tinggi. Berdasarkan hasil pengujian tarik didapatkan hasil tegangan tarik pada bevel groove mencapai 464.483 N/mm2. Pada hasil penelitian berdasarkan hasil uji struktur makro terlihat HAZ pada las dengan bevel groove lebih kecil dibandingkan dengan v groove. Sehingga pada pengujian ini bevel groove didapatkan sebagai hasil pengelasan yang lebih baik daripada v groove. Berdasarkan pengujian kekerasan yang dilakukan pada baja SA36 dengan bentuk groove berbeda memunculkan hasil kekerasan yang berbeda pula dimana hasil dari v groove lebih rendah akan kekerasannya dibandingkan bevel groove.
=======================================================================================================
Development of science and technology (science and technology) precisely in today’s welding technology has been widely used widely in connecting rods in steel building construction and construction machinery. So that knowledge of welding technology is required to achieve compatibility between the desired result with the welding process may be done in order to obtain optimal results.
In this thesis the use of welding SMAW welding. One type of welded joints that need to be explored further is the connection with a groove weld v and bevel. Groove type selection is based on the tendency of the more common usage. Furthermore, to know the strength of the connection of these two forms of groove to observe the macrostructure and mechanical properties.
From the test results that have been done on the SMAW welding steel SA 36 with bevel groove shape is stronger than v groove due to the tensile strength values obtained in the form of higher bevel groove. Based on the results of tensile test results obatained on the bevel groove tensile stress reaches 464.483 N/mm2. Based on test results shows that the macrostructure test looks HAZ on welding with bevel groove is smaller than the v groove. So at this testing bevel groove weld is obtained as a result better than the v groove. Based on hardness testing performerd on SA36 steel with grooves of different forms of violence that led to different results in wich the results of the v groove would lowe hardness than the bevel groove.
| Item Type: | Thesis (Diploma) |
|---|---|
| Additional Information: | RSMI 671.521 2 Ali p 3100018076188 |
| Uncontrolled Keywords: | IPTEK, Pengelasan, SMAW, Bevel Groove, V Groove, Sifat Mekanik, Science and Technology, Welding, SMAW, Bevel Groove, V Groove, Mechanical Properties |
| Subjects: | T Technology > TS Manufactures > TS227 Welding. |
| Divisions: | Faculty of Vocational > Mechanical Industrial Engineering (D4) |
| Depositing User: | Moch. Farobi Aliviyan |
| Date Deposited: | 16 Jan 2019 07:24 |
| Last Modified: | 04 Feb 2021 06:59 |
| URI: | http://repository.its.ac.id/id/eprint/57898 |