Analisis Pengaruh Variasi Temperatur dan Waktu Tahan Tempering terhadap Kekerasan Baja Assab 705 Yang Di-Hardening untuk Aplikasi Poros Pompa Multistage

Azizi, Muhamad Junda (2019) Analisis Pengaruh Variasi Temperatur dan Waktu Tahan Tempering terhadap Kekerasan Baja Assab 705 Yang Di-Hardening untuk Aplikasi Poros Pompa Multistage. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02511540000045-Undergraduate_Theses.pdf]
Preview
Text
02511540000045-Undergraduate_Theses.pdf - Accepted Version

Download (6MB) | Preview

Abstract

Pompa merupakan mesin fluida untuk memindahkan zat cair ke tempat yang diinginkan. Pompa beroperasi dengan membuat perbedaaan tekanan antara bagian masuk (suction) dengan bagian keluar (discharge). Pada Pabrik Gula Gending, normalnya rata-rata umur pakai poros pompa multistage adalah empat tahun. Akan tetapi ditemui kegagalan pada poros pompa yang baru berumur beberapa bulan dari 4 tahun umur pakai yang direncanakan. Kegagalan pada poros tersebut adalah patah dan aus pada ulirnya. Berdasarkan ASTM A291, material standar untuk poros tersebut adalah ASSAB 705. Namun pengujian komposisi dan kekerasan menunjukkan bahwa poros pompa tersebut tidak memenuhi standar. Untuk memperbaiki sifat mekanik, dilakukan penelitian mengenai pengaruh variasi parameter perlakuan panas tempering terhadap baja ASSAB 705 untuk aplikasi poros pompa. Perlakuan yang diberikan adalah water quench hardening dengan temperatur 815oC dan waktu tahan 30 menit. Kemudian dilakukan tempering dengan temperatur 300oC, 350oC dan 400 oC dimana variasi waktu tahan tiap temperatur tersebut adalah 60 menit dan 120 menit. Pengujian metalografi menunjukkan bahwa semakin tinggi temperatur dan waktu tahan, martensit tampak semakin sedikit akibat terdekomposisi menjadi struktur ferrit dan bainit. Pengujian XRD menunjukkan berkurangnya struktur BCT (martensit) seiring bertambahnya struktur BCC (bainit dan ferrit) pada temperatur dan waktu tahan yang makin tinggi. Spesimen dengan kekerasan dan ketahanan aus tertinggi adalah yang diberikan tempering dengan temperatur 300oC dan waktu tahan 60 menit. Sedangkan yang memiliki kekerasan dan ketahanan aus paling rendah adalah yang diberikan tempering dengan temperatur 400oC dan waktu tahan 120 menit.
===============================================================================================
Pump is a fluid machine to move liquid which operates with making pressure gradient between suction side and discharge side. It means that pump converts mechanical energy to flow the liquid. In Gending Sugar Company, multistage pump shaft can normally operates for 4 years lifetime. But, there is a multistage pump shaft failure after only few months operating period. This shaft failure is fracture and screw surface wear out. According to ASTM A291, the material of this shaft should be ASSAB 705. However, spectroscopy and hardness test shows that this shaft is not suitable to used as multistage pump shaft. To improve the mechanical properties, heat treatment is necessary. So, this experiment is about heat treating ASSAB 705 steel. The heat treatment is water-quench hardening with temperature 815oC in 30 minutes. Then the steel tempered with temperature 300oC, 350oC and 400oC in 60 minutes and 120 minutes for each temperature. Metallography test shows that higher the tempering temperature and holding time, the martensite is fewer because it decomposed to ferrite and bainite. XRD test shows the corresponding result in the decreasing of BCT structure (martensite) as BCC structure (ferrite and bainite) increase in the higher tempering temperature and holding time. This phenomena affect the hardness and wear resistant of the steel. Speciment with highest hardness and wear resistant is the 300oC-60 minutes tempered ASSAB 705 steel. While the specimen with lowest hardness and wear resistant is the 400_C-120 minutes tempered ASSAB 705 steel.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.36 Azi a-1 2019
Uncontrolled Keywords: Poros Pompa Multistage, ASSAB 705, Perlakuan Panas, Kekerasan, Keausan
Subjects: T Technology > TJ Mechanical engineering and machinery > TJ903 Pumping machinery.
T Technology > TJ Mechanical engineering and machinery > TJ910 Electric pumping machinery
T Technology > TN Mining engineering. Metallurgy > TN687 Electric furnaces.
T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Muhamad Junda Azizi
Date Deposited: 02 Jun 2021 07:16
Last Modified: 06 Aug 2021 07:00
URI: http://repository.its.ac.id/id/eprint/60256

Actions (login required)

View Item View Item