Analisis Pengaruh Campuran Coating Epoxy Dan Aluminium Serbuk Dengan Variasi Sudut Terhadap Kekuatan Adhesi, Mofologi, Dan Prediksi Laju Korosi Pada Baja Astm A36

Ali, Muhammad Sulton (2019) Analisis Pengaruh Campuran Coating Epoxy Dan Aluminium Serbuk Dengan Variasi Sudut Terhadap Kekuatan Adhesi, Mofologi, Dan Prediksi Laju Korosi Pada Baja Astm A36. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 04311440000106_undergraduate_thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2023. Download (11MB) | Request a copy

Abstract

Permasalahan korosi merupakan masalah utama penyebab terjadinya kegagalan pada material terutama pada bangunan laut, dimana biasanya ditempatkan pada kondisi atau lingkungan yang korosif. Salah satu langkah preventif yang digunakan untuk memperlambat korosi pada suatu material adalah dengan metode pelapisan atau coating. Pada penelitian ini menggunakan material ASTM A36. Baja ini dijadikan bahan uji karena baja ASTM 36 baja yang sering dijadikan material pada bangunan laut. Metode yang digunakan untuk penelitian adalah dengan memvariasikan sudut blasting dengan coating yang digunakan adalah campuran epoxy dan aluminium serbuk. Variasi campuran coating nya yaitu 10% aluminium serbuk ditambah epoxy, 20% aluminium ditambah epoxy dan 30% aluminium ditambah epoxy. Yang pertamana baja ASTM A36 dipotong menjadi 18 spesimen kemudian coating dilapiskan ke tiap-tiap spesimen dengan campuran aluminium yang sudah divariasikan. Setelah itu ke enam spesimen tersebut diuji kekuatan adhesi dan diuji yang kedua untuk mendapatkan prediksi laju korosi. Pada pengujian Pull-Off nilai terbaik dimiliki oleh spesimen dengan variasi penambahan aluminium serbuk 10% dan variasi sudut blasting 90° dengan nilai sebesar 14.9367 MPa. Sedangkan pada pengujian sel tiga elektroda menunjukkan bahwa ketahanan korosi terbaik didapat pada spesimen dengan penambahan aluminium 30% dan variasi sudut blasting 90° dengan nilai sebesar 0,00008567 mmpy. Untuk pengujian SEM menunjukkan bahwa terlihat pigmen aluminium yang berbentuk platey atau lamellar dan terlihat persebaran aluminium serbuk dipermukaan sampel yang merata.
================================================================================================
The problem of corrosion is a major problem the cause of the failure on the building material, especially in the sea, which is usually placed on the conditions or corrosive environments. One of the preventive measures that are used to slow the rate of corrosion of the material is the method of coating. In this study, using material ASTM A36. This steel is used as the test material for steel ASTM 36 steel is often used as a building material at sea. The method used for the study is by varying the angle of blasting coating. coatings used is a mixture of epoxy and aluminum powder. Variation its coating mixture that is 10% aluminum powder plus epoxy, epoxy plus 20% aluminum and 30% aluminum plus epoxy. The first of ASTM A36 steel is cut into 18 specimens then coating superimposed onto each specimen with a mixture of aluminum that has been varied. After that the 18 specimens that tested the strength of adhesion and the second test to get a prediction of the rate of corrosion. Pull-Off on testing best value owned by the specimen with a variation of 10% addition of aluminum powder and blasting a 90 ° angle variation in the amount of 14.9367 MPa. While the three-electrode cell testing shows that the best corrosion resistance obtained on the specimen with the addition of aluminum 30%, and variation blasting angle of 90 ° with a value of 0.00008567 mmpy. For SEM examination showed that the visible-shaped aluminum pigments or lamellar platey and visible distribution of aluminum powder on the surface of the sample prevalent.

Keyword : Steel ASTM A36, Coating Epoxy, Corrosion, Aluminium, Adhesion, Corrotion, Morfology.

Item Type:	Thesis (Undergraduate)
Additional Information:	RSKe 620.112 23 Ali a-1 2019
Uncontrolled Keywords:	Steel ASTM A36, Coating Epoxy, Corrosion, Aluminium, Adhesion, Corrotion, Morfology.
Subjects:	Q Science Q Science > QD Chemistry > QD115 Electrochemical analysis Q Science > QD Chemistry > QD383 Epoxy Compounds T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions:	Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User:	Muhammad Sulton Ali
Date Deposited:	20 Sep 2021 06:07
Last Modified:	20 Sep 2021 06:07
URI:	http://repository.its.ac.id/id/eprint/60520

Actions (login required)

View Item