Santoso, Adianto Hibatullah (2015) Pengaruh Beban Terhadap Laju Korosi Lapisan Baja Galvalum (Zn55Al) di Lingkungan Air Ledeng Dan Air Laut. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2711100048-Presentation.pdf - Presentation Download (3MB) | Preview |
Preview |
Text
2711100048-Paper.pdf - Published Version Download (580kB) | Preview |
Preview |
Text
2711100048-Undergraduate_Theses.pdf - Published Version Download (6MB) | Preview |
Preview |
Text
2711100048-Presentation 2.pdf - Presentation Download (3MB) | Preview |
Abstract
Baja galvalum memiliki sejarah sebagai rangka atap
pada konstruksi bangunan yang efektif dan ekonomis. Baja
galvalum terdiri dari lapisan tipis seng dan aluminium yang
menyatu pada substrat baja ringan. Paduan lapisan baja
galvalum memberikan perlindungan galvanik yang sangat
baik dan laju korosi yang rendah. Rangka atap yang berada
pada rumah mendapatkan beban yang berbeda. Beban dari
rangka atap bergantung pada beban mati, beban hidup
terbagi rata, beban hidup terpusat dan beban angin. Rumah
dapat berada dalam kawasan tepi pantai maupun berada
pada perkotaan sehingga adanya pengujian salt spray
dengan tujuan untuk mendapatkan simulasi lingkungan yang
dekat dengan laut dan pengujian dengan immerse air ledeng
bertujuan untuk mendapatkan simulasi lingkungan perkotaan
dan jauh dari laut. Penelitian ini dilakukan untuk
mempelajari laju korosi pada spesimen baja galvalum yang
diberi variasi beban 0, 20, 30, dan 40 % tegangan luluh
dalam media air ledeng dan NaCl 5% selama 10, 20, 30, 40
dan 50 hari dengan temperatur 300C. Hasil korosi
dikarakterisasi menggunakan XRD, SEM, dan polarisasi
tafel. Hasil pengujian menunjukkan bahwa dengan bertambahnya beban, maka laju korosi pada baja galvalum
akan meningkat. Air garam lebih korosif daripada air ledeng.
Sedangkan dengan bertambahnya waktu, maka laju korosi
baja galvalum akan menurun. Hal ini karena produk korosi
seng dan aluminium mengendap di permukaan. Hasil
pengujian XRD ditemukan senyawa Zinc Hydroxide
Zn(OH)2, Zinc Oxide (ZnO), Aluminium hydroxide
(Al(OH)3), Aluminium Hydroxide Oxide (AlOOH), dan
Aluminium Oxide (Al2O3). Dari pengujian SEM, ditemukan
daerah gelap yaitu fasa yang kaya akan seng dan daerah
terang yaitu fasa kaya akan aluminium. ========== Galvalume steel has been used effectively and
economically as roof trusses in building construction
throughout history. Galvalume steel consists of a thin layer
of zinc and aluminum which are fused on mild steel substrate.
Galvalum layer provides excellent galvanic protection and
lower corrosion rate. Roof truss used in a home received
different amount of loads. The loads received by the roof truss
are dead load, distributed live load, centralized live load and
load caused by wind. The house might be located in coastal
areas and urban areas hence it needed to simulate using sea
water and simulate urban environment using natural fresh
water. The purpose of this research is to study the corrosion
rate of the galvalume steel which is given the load variation
of 0, 20, 30, 40 % yield strength of the medium fresh water
and NaCl 5% for 0, 10, 20, 30, 40 and 50 days with a
temperature of 300C . Corrosion characterization were
analyzed using XRD, SEM, and Tafel polarization. The result
of this study, showed that the corrosion rate of galvalume
layer increased in accordance with the load applied. Salt
water more corrosive than natural fresh water. Whereas the increasing time would decrease the corrosion rate. This
happened because the corrosion products, zinc and
aluminum, settled on the surface. From the XRD results, we
founded Zinc Hydroxide Zn(OH)2, Zinc Oxide (ZnO),
Aluminium hydroxide (Al(OH)3), Aluminium Hydroxide
Oxide (AlOOH), dan Aluminium Oxide (Al2O3) compounds,
and from SEM, we obtained darker area which is a phase rich
in zinc and the lighter area, which is a phase rich in
aluminum.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSMt 620.112 23 San p |
| Uncontrolled Keywords: | Baja Galvalum, Zn55Al, Laju Korosi, Air Ledeng, Air Laut, Galvalume Steel, Zn55Al, Corrosion Rate, Fresh Water, Sea Water |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | - Davi Wah |
| Date Deposited: | 19 Mar 2019 06:47 |
| Last Modified: | 19 Mar 2019 06:49 |
| URI: | http://repository.its.ac.id/id/eprint/62538 |
Actions (login required)
 |
View Item |