Widianti, Ika Silviana (2015) Pengaruh Variasi pH Dan Temperatur Sintering Terhadap Nilai Sensitivitas Material TiO2 Sebagai Sensor Gas CO. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2711100065-Undergraduate_Theses.pdf - Published Version Download (2MB) | Preview |
Preview |
Text
2711100065-Presentation.pdf - Presentation Download (2MB) | Preview |
Preview |
Text
2711100065-Paper.pdf - Published Version Download (691kB) | Preview |
Abstract
Telah dilakukan berbagai macam pengupayaan untuk
mengoptimalkan potensi Titanium dioksida (TiO2) sebagai sensor
gas, mengingat TiO2 merupakan semikonduktor metal oksida.
Pada penelitian ini digunakan TiO2 dalam bentuk serbuk, dengan
pelarutnya H2SO4 yang diencerkan dengan air distilasi sehingga
terbentuk variasi pH 1, 3, dan 5. Metode sol-gel dilakukan dengan
perendaman dan dilanjutkan stiring selama 2,5 jam, kecepatan
700 rpm, dan temperatur 200ºC . Drying dilakukan selama 2 jam
pada temperatur C, selanjutnya serbuk dikompaksi pada
tekanan 200 bar agar terbentuk pellet. Pelet kemudian disintering
pada temperatur 700ºC, 800ºC, dan 900ºC selama 1 jam.
Karakterisasi material dilakukan dengan Scanning Electron
Microscope (SEM) dan X-Ray Diffraction (XRD). Sedangkan
untuk luas permukaan spesifik sampel TiO2 diuji dengan BET
Analyser. Morfologi TiO2 yang dihasilkan dari proses sol-gel
berbentuk bulat (spherical) dan memiliki ukuran kristal 69,74 nm.
Nilai sensitivitas didapatkan dari pengujian sensitivitas pada
temperatur 100ºC dan variasi volume gas CO 5L, 12,5L, 25L.
Respon terbaik adalah material TiO2 pH 3 yang disinter dengan
temperatur 900ºC, serta memiliki ukuran pori 50,83 nm. ========== It has been done various efforts to optimize titanium
dioxide (TiO2) potential as a gas sensor material, since TiO2 is a
semiconductor metal oxide. In this research TiO2 powder is used
with H2SO4 as the solvent dissolved in distilled water to make
various pH such as 1,3, and 5. The sol-gel method is done through
submersion and samples is stirred 2,5 hours with 700 rpm speed,
and 200ºC until the gel formed. Drying process is done by 2 hours
holding at 350ºC, then the powder is compacted with 200 bar
pressure to make pellets. Pellets are sintered at 700, 800, 900ºC
for 1 hour. Material characterization is done by using Scanning
Electron Microscope (SEM) and X-Ray Diffraction (XRD).
Meanwhile, to identify spesific surface area of the TiO2 sample is
tested using BET Analyser. The morphology of TiO2 by using
sol-gel method are spherical in shape and have 69,74 nm crystal
size. Sensitivity values are got from sensitivity test on 100ºC and
variation of CO gas volume 5L, 12,5L, and 25L. The best
response is found on material TiO2 pH 3 which is sintered at
900ºC, and also has porous size of 50,83 nm .
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSMt 681.25 Wid p |
| Uncontrolled Keywords: | titanium dioksida (TiO2), pH, metode sol-gel, sintering, nilai sensitivitas, gas CO, titanium dioxide (TiO2), pH, sol-gel method, sinter, sensitivity value, CO gas |
| Subjects: | T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK7871.674 Detectors. Sensors |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | - Davi Wah |
| Date Deposited: | 21 Mar 2019 09:01 |
| Last Modified: | 21 Mar 2019 09:01 |
| URI: | http://repository.its.ac.id/id/eprint/62565 |