Studi Pengaruh Artificial Aging pada Paduan Aluminium 339 terhadap Struktur Mikro, Kekerasan, dan Kekuatan Untuk Aplikasi Piston MAHLE M142

Al Hamid, Iqbal Azka (2019) Studi Pengaruh Artificial Aging pada Paduan Aluminium 339 terhadap Struktur Mikro, Kekerasan, dan Kekuatan Untuk Aplikasi Piston MAHLE M142. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511540000003-Undergraduate-Theses.pdf Restricted to Repository staff only Download (12MB) | Request a copy

Abstract

Aluminium merupakan logam yang banyak digunakan oleh manusia karena sifatnya yang kuat, ringan, tahan korosi dan mudah dibentuk. Paduan aluminium berperan besar dalam penggunaanya di bidang industri otomotif. Komponen otomotif yang menggunakan paduan aluminium salah satunya adalah piston. Piston dituntut untuk memiliki kekuatan dan kekerasan yang baik, karena banyak kegagalan yang terjadi dalam dunia otomotif yang disebabkan pendeknya umur pemakaian piston akibat keausan yang terjadi pada piston. Penelitian bertujuan untuk mengetahui perubahan kekerasan, kekuatan, dan struktur mikro dari paduan aluminium 339 yang diberi perlakuan panas variasi temperatur dan waktu tahan. Penelitian diawali dengan proses pengecoran material aluminium dengan unsur paduan tambahan yaitu tembaga, sillikon, dan magnesium, kemudian dilakukan perlakuan panas artificial aging pada variasi temperatur sebesar 40°C, 80°C, dan 120°C dengan variasi waktu tahan 8,12,16 jam dan terakhir dilakukan pengujian komposisi, pengujian XRD, pengujian SEM, pengujian tarik, pengujian metalografi, dan pengujian kekerasan untuk mengetahui pengaruhnya. Perolehan hasil pengujian pada struktur mikro yaitu terbentuk presipitat Mg2Si yang mulai terlihat pada temperatur aging 120ºC, sedangkan perubahan sifat mekanik yang berupa kekerasan dan kekuatan tarik tertinggi terdapat pada paduan dengan temperatur aging 120ºC dan waktu tahan aging 16 jam sebesar 137,67 Mpa dan 140 HB.
===================================================================================================================================
Aluminum is widely used by humans because it is strong, lightweight, corrosion resistant and easily formed. Aluminum alloy have a major role in its use in the automotive industry. One of the Automotive components that use aluminum alloys is a piston. Pistons are required to have good mechanical properties, because many failures occur in the automotive world due to piston failure. The aim of this study was to determine changes in the hardness, strength, and microstructure of aluminum 339. pistons which were given heat treatment with temperature and time resistant variations. The research begins with the process of casting aluminum material with additional alloying elements namely copper, silicon and magnesium, then heat treatment of artificial aging in temperature variation of 40°C, 80°C, and 120°C with a variation of holding time 8,12,16 hour and the last was tested to find out the effect. The acquisition of the test results on the microstructure is formed Mg2Si precipitate which began to be seen at an aging temperature of 120ºC, while the change in mechanical properties in the form of hardness and highest tensile strength was found in alloys with an aging temperature of 120ºC and a 16-hour aging resistance of 137.67 Mpa and 140 HB .

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Aluminium 339, Artificial Aging, Perlakuan Panas, Kekuatan, Kekerasan, Struktur Mikro
Subjects:	T Technology > TS Manufactures > TS170 New products. Product Development
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Iqbal Azka Al Hamid
Date Deposited:	22 Jul 2026 05:58
Last Modified:	22 Jul 2026 05:58
URI:	http://repository.its.ac.id/id/eprint/64976

Actions (login required)

View Item