Analisis Sour Corrosion Pada Baja ASTM A36 Akibat Pengaruh Asam Sulfat Dengan Variasi Temperatur Dan Waktu Perendaman Di Lingkungan Laut

Baihaqi, Ray Adam (2019) Analisis Sour Corrosion Pada Baja ASTM A36 Akibat Pengaruh Asam Sulfat Dengan Variasi Temperatur Dan Waktu Perendaman Di Lingkungan Laut. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 04311540000045-Undergraduate_Theses.pdf Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Pada industri maritim masalah korosi merupakan masalah yang serius yang terjadi pada logam karena bisa mengurangi nilai ekonomis dari logam tersebut. Logam yang paling banyak digunakan pada industri maritim adalah Baja ASTM A36 yang merupakan baja karbon rendah dengan kandungan karbon 0,25% sampai 0,29%. Tujuan penelitian ini untuk mengetahui variasi medium perendaman, temperatur dan waktu perendaman terhadap laju korosi Baja ASTM A36. Pada medium perendaman menggunakan dua variasi yaitu medium NaCl 3,5% yang merupakan medium air laut buatan dan medium NaCl 3,5% + H2SO4 0,5 M. Kemudian untuk variasi temperatur adalah 20˚, 30˚, 40˚ C. Dan variasi waktu perendaman yang digunakan 24, 72, 120 dan 168 jam. Hasil dari uji immersion corrosion test menunjukkan nilai laju korosi tertinggi terjadi pada Baja ASTM A36 yang direndam pada medium NaCl 3,5% + H2SO4 0,5 M dengan temperatur perendaman 40˚ C yang menunjukkan nilai laju korosi 37,584 mmpy (24 jam), 31,965 mmpy (72 jam), 23,795 mmpy (120 jam), 19,375 mmpy (168 jam), kemudian pada material sampel uji tersebut terjadi korosi seragam dan korosi batas butir. Nilai laju korosi tertinggi pada medium perendaman NaCl 3,5% terjadi pada Baja ASTM A36 yang direndam pada temperatur 40˚ C yang menunjukkan nilai laju korosi 0,098 mmpy (24 jam), 0,105 mmpy (72 jam), 0,081 mmpy (120 jam), 0,063 mmpy (168 jam), kemudian pada material sampel uji tersebut terjadi korosi seragam dan korosi sumuran. Hasil penelitian ini didapatkan adanya senyawa H2SO4 dan temperatur yang tinggi dapat mempercepat laju korosi di lingkungan laut.
=========================================================
In the maritime industry the problem of corrosion is a serious problem that occurs in metals because it can reduce the economic value of the metal. The most widely used metal in the maritime industry is ASTM A36 Steel which is low carbon steel with a carbon content of 0,25% to 0,29%. The purpose of this study was to determine the variation of immersion medium, temperature and time of immersion on the corrosion rate of ASTM A36 Steel. The immersion medium uses two variations, that is medium NaCl 3,5% which is an artificial sea water medium and medium NaCl 3,5% + H2SO4 0,5 M. Then for temperature variations are 20˚, 30˚, 40˚C. And the variation of immersion time used is 24, 72, 120 and 168 hours. The results of the immersion corrosion test showed that the highest corrosion rate occurred in ASTM A36 Steel which was immersed in medium NaCl 3,5% + H2SO4 0,5 M with an immersion temperature of 40˚ C which showed a corrosion rate of 37,584 mmpy (24 hours), 31,965 mmpy (72 hours ), 23,795 mmpy (120 hours), 19,375 mmpy (168 hours), then in the sample material the uniform corrosion and intergranular corrosion occur. The highest corrosion rate on medium NaCl 3,5% occurred in ASTM A36 Steel which was immersed at a temperature of 40˚ C which showed a corrosion rate of 0,098 mmpy (24 hours), 0,105 mmpy (72 hours), 0,081 mmpy (120 hours), 0,063 mmpy (168 hours), then on the test sample material uniform corrosion and pitting corrosion occur. The results of this study found the presence of H2SO4 compounds and high temperatures can accelerate the corrosion rate in the marine environment.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Korosi, Baja ASTM A36, Immersion Corrosion Test, Laju Korosi
Subjects:	T Technology > TC Hydraulic engineering. Ocean engineering > TC1665 Offshore structures--Materials.
Divisions:	Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User:	Ray Adam Baihaqi
Date Deposited:	26 May 2026 04:15
Last Modified:	26 May 2026 04:15
URI:	http://repository.its.ac.id/id/eprint/65040

Actions (login required)

View Item