Pengaruh Variasi Konsentrasi PLLA (Poly L-Lactic Acid) Sebagai Top Coat Terhadap Laju Degradasi Paduan Magnesium AZ31B Yang Dioksidasi Dengan PEO Untuk Aplikasi Biodegradable Orthopedic Devices

Prayogo, Muhammad Ihsan (2019) Pengaruh Variasi Konsentrasi PLLA (Poly L-Lactic Acid) Sebagai Top Coat Terhadap Laju Degradasi Paduan Magnesium AZ31B Yang Dioksidasi Dengan PEO Untuk Aplikasi Biodegradable Orthopedic Devices. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511540000109_undergraduate_theses.pdf - Accepted Version Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Penggunaan paduan magnesium sebagai biomaterial implan tulang telah menarik banyak perhatian untuk dikembangkan karena memiliki biodegradabilitas dan sifat mekanik yang menguntungkan. Namun, magnesium memiliki kekurangan yaitu laju degradasi yang cepat sehingga dibutuhkan coating agar dapat digunakan dalam jangka panjang sehingga sesuai dengan waktu penyembuhan tulang. Maka pada penelitian ini digunakan PLLA (Poly L-lactic acid) yakni polimer biodegradable yang diaplikasikan sebagai top coat dari paduan magnesium AZ31B yang telah dicoating dengan PEO (Plasma Electrolytic Oxidation). Variasi konsentrasi PLLA 2%, 4%, 6%, dan 8% yang dilarutkan dalam diklorometana akan diterapkan pada sampel untuk mengetahui dampak terhadap laju degradasi sampel dengan menggunakan dip coating. Pengujian SEM dilakukan untuk mengamati morfologi permukaan dan penampang melintang setiap specimen. Dari hasil pengamatan yang dilakukan semakin besar konsentrasi PLLA yang digunakan maka semakin kecil ukuran pori-pori pada permukaan dan semakin besar konsentrasi PLLA yang digunakan maka semakin tebal coating pada specimen. Hasil analisis uji kekerasan, indentasi menembus keseluruhan lapisan dari PLLA hingga menyentuh base metal. Maka dari itu dapat disimpulkan bahwa penambahan PLLA tidak memberikan pengaruh yang signifikan terhadap nilai kekerasanya. Analisis kekuatan rekat (adhesi strength) metode tape test menunjukkan bahwa kekuatan rekat akan semakin turun dengan semakin tinggi nya konsentrasi PLLA yang digunakan. Analisis laju degradasi menggunakan metode weight loss menunjukkan bahwa laju degradasi semakin rendah dengan tinggi nya konsentrasi PLLA yang digunakan. Hal ini dipengaruhi dengan hasil pengamatan morfologi gambar SEM yang menunjukkan bahwa pori-pori permukaan yang semakin kecil dengan tinggi nya konsentrasi PLLA yang digunakan. Untuk specimen dengan perlakuan PLLA 8% memiliki laju degradasi yang paling lambat atau bisa dikatan optimum dengan degradasi 2,1364 mm/tahun, laju degradasi ini menurun signifikan jika dibandingkan dengan AZ31B tanpa perlakuan yang laju degradasi nya 6,3966 mm/tahun dan AZ31B yang hanya di PEO yang laju degradasi nya 4,6105 mm/tahun.
====================================================================================================================================
The usage of magnesium as a biomaterial for bone implants has attracted much attention to be developed because it has beneficial biodegradability and mechanical properties. However, magnesium has a disadvantage that is the high rate of degradation, so surface modification or coating is required for the long-term use match with the time of bone recovery. So in this study PLLA (Poly L-lactic acid), which is a biodegradable polymer, is applied as a top layer of AZ31B magnesium alloy which was coated with PEO (Plasma Electrolytic Oxidation). Variations in PLLA concentration of 2%,4%,6%, and 8% dissolved in dichloromethane will be applied to the sample to obtain an effect on the degradation rate of the sample using dip coating. SEM testing was carried out to observe the surface and cross-section appearance of each specimen. From the observation showed that the greater PLLA concentration used, the smaller pores size on the surface and the greater PLLA concentration used, the thicker layer on the specimen. The results of the hardness test analysis, indentation penetrate all layers of the PLLA through the base metal. So it can be concluded that PLLA does not give a significant effect to hardness property. Adhesion strength analysis with tape test method showed that the adhesive strength will decrease with increasing of PLLA concentration used. The degradation rate analysis with weight loss method showed that the degradation rate will decrease with increasing of PLLA concentration used. This thing is supported by the results of SEM morphological observation that shows the greater PLLA concentration used, the smaller pores size on the surface. For specimens with PLLA 8% has the slowest degradation rate with degradation of 2,1364 mm / year, this degradation rate decrease significantly compared to AZ31B base metal which can accelerate degradation rates of 6,3966 mm / year and AZ31B which is only coated with PEO the degradation rate is 4,6105 mm / year.

Item Type:	Thesis (Other)
Additional Information:	RSMt 620.112 6 Pra p-1 2019 3100019081619
Uncontrolled Keywords:	Biodegradable, Dip coating, Magnesium AZ31B, Plasma Electrolytic Oxidation, Poly L-lactic acid
Subjects:	T Technology > T Technology (General) T Technology > TA Engineering (General). Civil engineering (General) > TA491 Metal coating. T Technology > TS Manufactures > TS699 Powder coating of metals
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Muhammad Ihsan Prayogo
Date Deposited:	19 Dec 2025 04:33
Last Modified:	19 Dec 2025 04:33
URI:	http://repository.its.ac.id/id/eprint/65471