Analisa Distribusi Temperatur dan Tegangan Termal pada Cetakan Beda Material dalam Proses Injection Molding Metode Rapid Heat Cycle Molding menggunakan Metode Elemen Hingga

Anura, Kharisma Putra (2019) Analisa Distribusi Temperatur dan Tegangan Termal pada Cetakan Beda Material dalam Proses Injection Molding Metode Rapid Heat Cycle Molding menggunakan Metode Elemen Hingga. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511540000093_Undergraduate_theses.pdf Restricted to Repository staff only Download (4MB) | Request a copy

Abstract

Injection molding merupakan salah satu jenis manufaktur yang dapat digunakan untuk menghasilkan bermacam – macam produk dari polimer. Kelebihan dari proses ini ialah dapt menghasilkan produk dengan cepat dan dengan dimensi yang komplek. Untuk mempercepat proses pembuatan produk dan meningkatkan kualitasnya ditelitilah sebuah metode, yaitu Rapid Heat Cycle Molding (RHCM). Cara kerja metode ini yaitu memanaskan cetakan diatas temperatur glass dan mendinginkan cetakan dengan cepat. Tujuan penelitian ini ialah untuk membandingkan distribusi temperatur, tegangan termal dan cycle time menggunakan material cetakan yang berbeda. Material cetakan yang dibandingkan adalah Al 7075 dan S136. Dengan menggunakan software permodelan ANSYS dengan metode perhitungannya mengguanakan Finite Element Methode (FEM) diperoleh hasil berupa distribusi temperatur pada proses injeksi molding hanya berpengaruh pada lamanya heating dan cooling sedangkan untuk mendapatkan temperatur yang seragam pada permukaan cavity diperlukan desain sistem pemanas dan pendingin yang baik , tegangan termal cetakan aluminium sebesar 71 MPa dan cetakan baja memiliki tegangan termal maksimum sebesar 1 MPa, dan waktu cycle yang dihasilkan dari proses simulasi pada cetakan aluminium adalah 13 detik untuk cycle ke-1 dan ke-2 sedangkan baja 23 detik untuk cycle ke-1 dan 19 detik untuk cycle ke-2.
===================================================================================================================================
Injection molding is one type of manufacturing that can be used to produce a variety of products from polymers. The advantage of this process is that it can produce products quickly and with complex dimensions. To speed up the process of making products and improve their quality, a method namely Rapid Heat Cycle Molding (RHCM) was discovered. The way this method works is to heat the mold above the glass temperature and cool the mold quickly. The purpose of this study is to compare the temperature distribution, thermal stress and cycle time / time needed to make a product using different materials mold. The material mold compared is Al 7075 and S136. By using ANSYS modeling software with its calculation method using Finite Element Methode (FEM), obtained result in the form of temperature distribution in the injection molding process will affect the duration of heating and cooling while to obtain a uniform temperature at the cavity surface a good heating and cooling system design is needed, thermal stress of aluminum mold is 71 MPa and steel mold has a maximum thermal stress of 1 MPa, and the cycle time generated from the simulation process on aluminum mold is 13 seconds for the 1st and 2nd cycle while the steel mold is 23 seconds for the 1st and 19 seconds cycles for the 2nd cycle.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Injection Molding, Rapid Heat Cycle Molding, Metode Elemen Hingga
Subjects:	T Technology > TS Manufactures > TS171 Product design T Technology > TS Manufactures > TS176 Manufacturing engineering. Process engineering (Including manufacturing planning, production planning) T Technology > TS Manufactures > TS2301.T7 Toys, etc
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Kharisma Putra Anura
Date Deposited:	22 Jul 2026 07:33
Last Modified:	22 Jul 2026 07:33
URI:	http://repository.its.ac.id/id/eprint/65591

Actions (login required)

View Item