Sintesis IRMOF-3 Dengan Penambahan γ-Al2O3 Serta Kinerjanya Sebagai Katalis Esterifikasi Asam Oleat Dengan Metanol

Sanjaya, Anis (2019) Sintesis IRMOF-3 Dengan Penambahan γ-Al2O3 Serta Kinerjanya Sebagai Katalis Esterifikasi Asam Oleat Dengan Metanol. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01211540000091-Undergraduate_Theses.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Pada penelitian ini IRMOF-3 telah disintesis dengan penambahan γ-Al2O3 pada variasi massa sebesar 2,5%, 5% dan 10% secara solvotermal pada suhu 100°C selama 24 jam Hasil sintesis dikarakterisasi dengan instrumen XRD, FTIR, SEMEDX, TGA, dan Adsorpsi-desorpsi N2. Difraktogram semua padatan hasil sintesis memiliki puncak-puncak karakteristik yang sama dengan IRMOF-3 standar. Hasil analisis dengan SEM menunjukkan bahwa IRMOF-3 hasil sintesis memiliki morfologi permukaan berbentuk kubik, akan tetapi penambahan γ-Al2O3 menyebabkan perubahan morfologi permukaan menjadi lebih kasar. Hasil EDX menunjukkan persebaran unsur C, N, O, Al, dan Zn yang merata pada komposit. Penambahan γ-Al2O3 menghasilkan komposit dengan stabilitas termal dan jari-jari pori lebih tinggi dibandingkan dengan IRMOF-3 serta luas permukaan dan volume pori yang lebih tinggi pula. Hasil reaksi esterifikasi asam oleat dengan metanol pada rasio minyak:alkohol 1:30 dalam waktu 2 jam memberikan konversi FFA sebesar 22,93%dengan katalis IRMOF-3. Pada kondisi yang sama, konversi FFA mencapai 57,73% pada reaksi esterifikasi dengan katalis Al(10)IRMOF-3.
===================================================================================================================================
**English Version (without paragraphs):**

In this study, IRMOF-3 was successfully synthesized using the solvothermal method at 100°C for 24 hours with the addition of γ-Al₂O₃ at mass loadings of 2.5%, 5%, and 10%. The synthesized materials were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy (SEM-EDX), thermogravimetric analysis (TGA), and N₂ adsorption-desorption analysis. The XRD diffractograms of all synthesized samples exhibited characteristic peaks at 2θ corresponding to those of the reference IRMOF-3, confirming the successful formation of the framework. SEM observations showed that the synthesized IRMOF-3 possessed a cubic surface morphology, while the incorporation of γ-Al₂O₃ produced a rougher surface morphology. EDX analysis confirmed the homogeneous distribution of C, N, O, Al, and Zn elements throughout the composite materials. Furthermore, the addition of γ-Al₂O₃ enhanced the thermal stability, pore diameter, specific surface area, and pore volume of the composites compared with pristine IRMOF-3. The esterification of oleic acid with methanol at an oil-to-alcohol molar ratio of 1:30 for 2 hours resulted in a free fatty acid (FFA) conversion of 22.93% using IRMOF-3 as the catalyst. Under the same reaction conditions, the FFA conversion increased to 57.73% when Al(10)IRMOF-3 was used as the catalyst.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	IRMOF-3, γ-Al2O3, Solvotermal, Esterifikasi
Subjects:	Q Science > QD Chemistry Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Anis Sanjaya
Date Deposited:	20 Jul 2026 06:48
Last Modified:	20 Jul 2026 06:48
URI:	http://repository.its.ac.id/id/eprint/65933

Actions (login required)

View Item