SINTESIS NANOPARTIKEL Fe2TiO5 BERBASIS BAHAN ALAM BATU BESI DENGAN VARIASI WAKTU GILING

Julianitasari, Dwi (2019) SINTESIS NANOPARTIKEL Fe2TiO5 BERBASIS BAHAN ALAM BATU BESI DENGAN VARIASI WAKTU GILING. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111540000056-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

Sintesis nanopartikel Fe2TiO5 dari bahan dasar batu besi sebagai sumber Fe telah berhasil dilakukan dengan menggunakan kombinasi metode disolusi dan kopresipitasi. Sumber Fe adalah batu besi Kalimantan Selatan, sementara sumber Ti adalah TiO2 bahan komersial. Batu besi dimurnikan dengan metode disolusi, kopresipitasi dan dikalsinasi 800oC untuk menghasilkan serbuk Fe2O3 yang kemudian dicampur menggunakan Planetary Ball Mill dilanjutkan kalsinasi pada temperatur 1100oC untuk memperoleh serbuk Fe2TiO5. Selanjutnya serbuk Fe2TiO5 dilakukan variasi waktu penggilingan 0, 10, 15, 20, 25 jam untuk mendapatkan serbuk berukuran nanometer. Serbuk Fe2TiO5 dikarakterisasi menggunakan X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) dan UV-Vis Spectroscopy. Analisis data XRD menunjukkan bahwa fasa tunggal Fe2TiO5 (pseudobrookite) tetap bertahan untuk semua sampel variasi giling. Sementara itu, ukuran kristal yang dihasilkan cenderung semakin kecil seiring lamanya waktu penggilingan. Ukuran kristal paling kecil diperoleh saat waktu giling 15 jam, yaitu 64 nm. Hal ini didukung dengan hasil uji SEM, yaitu persebaran serbuk Fe2TiO5 giling 15 jam memiliki distribusi yang homogen. Sementara itu, analisis UV-Vis menunjukkan bahwa Fe2TiO5 dengan waktu penggilingan lebih lama mempunyai solubilitas yang tinggi, sehingga kemampuan mengabsorbsi cahaya juga akan semakin meningkat. Absorbansi meningkat hampir 15 kali ketika bubuk 25 jam diterapkan dibandingkan dengan serbuk yang tidak digiling.
=================================================================================================================================
The synthesis of Fe₂TiO₅ nanoparticles using ironstone as the iron source was successfully carried out through a combination of dissolution and coprecipitation methods. Ironstone obtained from South Kalimantan served as the Fe source, while commercial TiO₂ powder was used as the Ti source. Initially, the ironstone was purified by dissolution and coprecipitation, followed by calcination at 800°C to produce Fe₂O₃ powder. The resulting Fe₂O₃ powder was then mixed with TiO₂ powder and calcined at 1100°C to synthesize Fe₂TiO₅ powder. The successful formation of the Fe₂TiO₅ phase was confirmed by X-ray diffraction (XRD). Subsequently, the Fe₂TiO₅ powder was milled for 0, 10, 15, 20, and 25 hours to obtain nanometer-sized particles. The milled powders were characterized using XRD, Scanning Electron Microscopy (SEM), and UV–Vis spectroscopy. XRD analysis indicated that the single-phase Fe₂TiO₅ structure was retained after all milling durations, while the crystallite size generally decreased with increasing milling time. The sample milled for 15 hours exhibited the smallest crystallite size of 64 nm and the most homogeneous size distribution. UV–Vis spectroscopy of the powder dispersed in water showed that smaller crystallite sizes produced higher optical absorption. The absorbance increased by nearly 15 times for the powder milled for 25 hours compared with the unmilled sample.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Batu besi, Nanopartikel, Serbuk Fe2TiO5, Variasi waktu giling, Absorbansi.
Subjects:	Q Science > QC Physics > QC765 Magnetic materials
Divisions:	Faculty of Natural Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Dwi Julianitasari
Date Deposited:	20 Jul 2026 03:17
Last Modified:	20 Jul 2026 03:17